強く冷間圧延したステンレス鋼と特異的な機械的性質で開発された不均一ナノ構造【Powered by NICT】

Heterogeneous nanostructure developed in heavily cold-rolled stainless steels and the specific mechanical properties

著者 (7件)： Miura H. (Department of Mechanical Engineering, Toyohashi University of Technology, Tempaku-cho, Toyohashi, Aichi, 441-8580, Japan) ,  Kobayashi M. (Department of Mechanical Engineering, Toyohashi University of Technology, Tempaku-cho, Toyohashi, Aichi, 441-8580, Japan) ,  Todaka Y. (Department of Mechanical Engineering, Toyohashi University of Technology, Tempaku-cho, Toyohashi, Aichi, 441-8580, Japan) ,  Watanabe C. (Faculty of Mechanical Engineering, Kanazawa University, Kakuma-machi, Kanazawa, Ishikawa, 920-1192, Japan) ,  Aoyagi Y. (Department of Finemechanics, Tohoku University, Sendai, Miyagi, 980-8579, Japan) ,  Sugiura N. (Steel Research Labs., Nippon Steel & Sumitomo Metal Corp.20-1 Shintomi, Futtsu, Chiba 293-8511, Japan) ,  Yoshinaga N. (Steel Research Labs., Nippon Steel & Sumitomo Metal Corp.20-1 Shintomi, Futtsu, Chiba 293-8511, Japan)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 133  ページ： 33-36  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ステンレス鋼は92%の圧下率まで冷間圧延した。安定オーステナイトステンレス綱中に発達したミクロ組織はラメラ双晶分域,剪断帯と低角ラメラ境界で構成された複雑な不均一ナノ構造であった。フェライトラメラとオーステナイトの不均一ナノ構造が交互に積層した,しかし,冷間圧延二相ステンレス鋼はより複雑になり,混合微細構造を示した。強く冷間圧延ステンレス鋼とこれに続く時効は圧延方向に垂直な2.6GPaを超える驚くべき高い引張強さを示し,圧延方向に沿って約2GPaであった。このような高強度一方も,5%以上の中程度の塑性伸びが達成された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 二相ステンレス鋼 ,  *ナノ構造 ,  引張強さ ,  *冷間圧延 ,  圧下率 ,  剪断帯 ,  *ステンレス鋼 ,  *圧延 ,  時効 ,  オーステナイト系ステンレス鋼 ,  塑性 ,  オーステナイト ,  双晶 ,  伸び ,  圧延方向 ,  機械的性質 ,  強度 ,  比率 ,  性質

著者キーワード (5件)： 不均一ナノ構造 ,  双晶 ,  超微細粒 ,  圧延 ,  機械的性質

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： 冷間圧延 ,  ステンレス鋼 ,  機械的性質 ,  開発 ,  不均一 ,  ナノ構造