Synthesis of Fe Nanoparticles via One-Step Reduction Method

著者 (9件)： Hu Ping (School of Metallurgy Engineering, Xi’ an University of Architecture and Technology) ,  Kang Lu (School of Metallurgy Engineering, Xi’ an University of Architecture and Technology) ,  Yang Jun (School of Metallurgy Engineering, Xi’ an University of Architecture and Technology) ,  Yang Fan (School of Metallurgy Engineering, Xi’ an University of Architecture and Technology) ,  Wang Kuaishe (School of Metallurgy Engineering, Xi’ an University of Architecture and Technology) ,  Du Jinjing (School of Metallurgy Engineering, Xi’ an University of Architecture and Technology) ,  Yang Zhanlin (School of Metallurgy Engineering, Xi’ an University of Architecture and Technology) ,  Cao Weicheng (Jinduicheng Molybdenum Co., Ltd) ,  Liu Dongxin (Jinduicheng Molybdenum Co., Ltd)
資料名： Xiyou Jinshu Cailiao yu Gongcheng  (Xiyou Jinshu Cailiao yu Gongcheng)
巻： 45  号： 12  ページ： 3112-3114  発行年： 2016年 
JST資料番号： W0563A  ISSN： 1002-185X  CODEN： XJCGEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： ナノ鉄粉体を,新しい方法によって調製した。過剰のクエン酸は620°Cで純相,結晶の高いΑ-FEを形成するのに役立つ。X線回折(XRD),透過型電子顕微鏡(TEM),振動試料磁力計(VSM)により,ナノ鉄粉体を特性化し,30NMの直径を有する球状のナノ粒子を生成した。磁気ヒステリシスループは,FE_2O_3ナノ粒子の飽和磁化が198.97A M2/KGであり,磁性材料として優れた磁気特性を有することを示した。一段階還元法で製造した粒径分布は狭く、制御性があり、プロセスは短く、大規模生産に用いることができる。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 飽和磁化 ,  可制御性 ,  キャラクタリゼーション ,  磁性材料 ,  X線回折 ,  ナノ粒子 ,  磁気的性質 ,  透過型電子顕微鏡 ,  磁気ヒステリシス ,  *鉄粉 ,  粒度分布 ,  脂肪族アルコール ,  脂肪族カルボン酸 ,  ヒドロキシ酸 ,  ポリカルボン酸
準シソーラス用語： 試料振動型磁力計 , 【Automatic Indexing@JST】

著者キーワード (5件)： Fe nanoparticles ,  one-step reduction ,  spherical shape ,  ferromagnetic behavior ,  magnetic materials

分類 (3件)： 塩基,金属酸化物  (CD01030Z) ,  酸化物結晶の磁性  (BM06050E) ,  磁性材料  (NA04040H)

物質索引 (1件)： クエン酸

タイトルに関連する用語 (4件)： 段階 ,  還元 ,  鉄粉 ,  調製