中断されたその場引張試験による粉末冶金Ti-Si合金の強化靭性化機構研究【Powered by NICT】

Strengthening-toughening mechanism study of powder metallurgy Ti-Si alloy by interrupted in-situ tensile tests

著者 (8件)： Ye X.X. (Joining and Welding Institute (JWRI), Osaka University, Japan) ,  Imai H. (Joining and Welding Institute (JWRI), Osaka University, Japan) ,  Shen J.H. (Joining and Welding Institute (JWRI), Osaka University, Japan) ,  Chen B. (Joining and Welding Institute (JWRI), Osaka University, Japan) ,  Han G.Q. (College of Materials Science and Engineering, Beijing University of Technology, China) ,  Umeda J. (Joining and Welding Institute (JWRI), Osaka University, Japan) ,  Takahashi M. (Joining and Welding Institute (JWRI), Osaka University, Japan) ,  Kondoh K. (Joining and Welding Institute (JWRI), Osaka University, Japan)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 694  ページ： 82-92  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 粉末冶金Ti-Si合金の強化靭性化機構は中断されたin-situ引張試験により調べた。作製したTi-Si合金が強く,延性である。滑り帯は主に溶質と粒界により遮断された。狭い変形帯,整列した低角粒界と双晶境界もこの閉塞に積極的な役割をplaid。歪硬化段階における交差滑りは引張と降伏強度の差値を低下させた。二段階強靭化機構を研究した(ネッキング開始は境界点)であった。ネッキング前均一変形期間において,歪適合性は粒界回転([0001]に沿って回転軸,[ 1100]および[ 1102]),高角度粒界回転,粒界滑りと小双晶変形によって改善された。ネッキング後の不均一変形の期間では,マイクロクラックの開始/合体は均一な応力分布により引きずられることが分かった。亀裂伝搬も密な結晶粒界と前面塑性結晶粒により抑制された。強度と靭性の総合的な分析は,処理,機械的性質およびTi合金の微細構造の間の関係に関する深い理解を提供した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： チタン合金 ,  変形双晶 ,  延性 ,  亀裂伝搬 ,  *粉末冶金 ,  *引張 ,  滑り帯 ,  微小亀裂 ,  降伏強さ ,  粒界滑り ,  歪硬化 ,  *靱性 ,  応力分布 ,  結晶粒界 ,  *引張試験

著者キーワード (4件)： チタン合金 ,  強化機構 ,  強靭化機構 ,  その場引張試験

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)