融着帯モデリングに基づく繊維とマトリックス間の界面強度の評価【Powered by NICT】

Evaluation of interfacial strength between fiber and matrix based on cohesive zone modeling

著者 (4件)： Budiman Bentang Arief (Mechanical Engineering Department, Institut Teknologi Bandung, Ganesha Street No. 10, Bandung 40132, Indonesia) ,  Takahashi Kosuke (Division of Mechanical and Aerospace Engineering, Hokkaido University, N13, W8, Kita-ku, Sapporo, Hokkaido 060-8628, Japan) ,  Inaba Kazuaki (Department of Transdisciplinary Science and Engineering, Tokyo Institute of Technology, 2-12-1 I6-10, Ookayama, Meguro-ku, Tokyo 152-8552, Japan) ,  Kishimoto Kikuo (Department of Transdisciplinary Science and Engineering, Tokyo Institute of Technology, 2-12-1 I6-10, Ookayama, Meguro-ku, Tokyo 152-8552, Japan)
資料名： Composites. Part A. Applied Science and Manufacturing  (Composites. Part A. Applied Science and Manufacturing)
巻： 90  ページ： 211-217  発行年： 2016年 
JST資料番号： E0231D  ISSN： 1359-835X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 凝集表面としてモデル化した繊維/マトリックス界面に及ぼす非剛体結合を考慮した界面強度の測定法を提示した。単繊維のフラグメンテーション試験から得られた繊維亀裂近傍の応力集中に焦点を当てて,光弾性で観測されたマトリックス中の応力輪郭は,特性長さを定義することにより,界面強度に関連付けることができた。応力輪郭と界面強度に及ぼす特性長さ間の関係を表す方程式を導出し,有限要素解析を用いて検証した。提案した測定法の主要な利点は,マトリックスの弾性変形内で起こる通常単繊維亀裂のみが界面強度の評価に必要であることであるが,飽和繊維フラグメンテーションは,従来法が必要である。ここでは,単一炭素繊維とエポキシ試験片を用いて実証した試料と,23.8MPaの平均界面強度を得ることに成功した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *界面 ,  亀裂 ,  弾性変形 ,  応力集中 ,  凝集 ,  炭素繊維 ,  光弾性 ,  *モデリング ,  試験片 ,  フラグメンテーション
準シソーラス用語： 有限要素解析 ,  単繊維 ,  非剛体 ,  *界面強度 ,  *融着帯モデリング , 【Automatic Indexing@JST】

著者キーワード (4件)： B界面/相間 ,  Bフラグメンテーション ,  B繊維/マトリックス結合 ,  C.粘着性界面のモデル化

分類 (2件)： ゴム・プラスチック材料  (HC04030W) ,  機械的性質  (YH02022L)

タイトルに関連する用語 (5件)： 融着帯モデリング ,  繊維 ,  マトリックス ,  界面強度 ,  評価