H13+Nbバーにおける多重層を持つ大規模不均一炭窒化物の生成機構【Powered by NICT】

Generating Mechanism of Large Heterogeneous Carbonitrides with Multiple Layers in H13 + Nb Bar

著者 (5件)： Xie You (State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, 30 Xueyuan Road, Haidian District, Beijing, 100083, P. R. China) ,  Cheng Guoguang (State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, 30 Xueyuan Road, Haidian District, Beijing, 100083, P. R. China) ,  Chen Lie (Xining Special Steel Co., Ltd., 52 Chaidamu West Road, Xining Qinghai, 810005, P. R. China) ,  Zhang Yandong (Xining Special Steel Co., Ltd., 52 Chaidamu West Road, Xining Qinghai, 810005, P. R. China) ,  Yan Qingzhong (Xining Special Steel Co., Ltd., 52 Chaidamu West Road, Xining Qinghai, 810005, P. R. China)
資料名： Steel Research International  (Steel Research International)
巻： 88  号： 1  ページ： ROMBUNNO.201600119  発行年： 2017年 
JST資料番号： A0446A  ISSN： 1611-3683  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： H13+Nb棒におけるミクロンサイズの不均一な炭窒化物の特性と発生機構を研究した。三種類の析出物は層,すなわち,二層,三層,四層の数に応じて観察された。二層析出物は酸化物コアと外側Ti-V-リッチの炭窒化物を含むが,三層析出物は外側にもう一つのNb炭窒化物を持っている。四層沈殿物を三層析出物のそれに類似した相の内三種類に加えて最外層でV炭窒化物を持っている。これらの大きな析出物のサイズは十μmにまですることができた。酸化物コアは主に化学量論的スピネルMgAl_2O_4と凝固前の液体鋼で発生した。炭窒化物の組成特性と沈殿配列をThermo-CalcのScheil-Gulliverモデルによる計算によって良く説明できた。Ti-V-リッチ相析出物は凝固中の最初の,その後Nbリッチ相とVリッチ相が連続的に析出した。温度低減し,加熱処理プロセス中の異なる層の間に起こるいくつかの溶解。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： スピネル ,  *ニオブ ,  *多層 ,  凝固 ,  析出物 ,  沈殿物 ,  溶鋼 ,  化学量論 ,  沈殿 ,  酸化物
準シソーラス用語： 加熱処理 ,  Thermo-Calc ,  二層 ,  *生成機構 ,  *炭窒化物 , 【Automatic Indexing@JST】

著者キーワード (5件)： 不均一析出 ,  炭窒化物 ,  層構造 ,  生成機構 ,  NbマイクロアロイドH13

分類 (1件)： 組織的硬化現象  (WB01020C)

タイトルに関連する用語 (4件)： 多重層 ,  大規模 ,  不均一 ,  炭窒化物