ポリ(L-ラクチド)/ポリメタクリル酸メチル/炭素充填材複合材料の電気的性質を変更するためのポリマ分解の利用

Utilization of polymer degradation to modify electrical properties of poly(l-lactide)/poly(methyl methacrylate)/carbon filler composites

著者 (5件)： BUYS Yose Fachmi (Dep. of Chemistry and Materials Sci., Tokyo Inst. of Technol., 2-12-1-S8-43 Ookayama, Meguro-Ku, Tokyo 152-8550, JPN) ,  AOYAMA Takehiko (Dep. of Chemistry and Materials Sci., Tokyo Inst. of Technol., 2-12-1-S8-43 Ookayama, Meguro-Ku, Tokyo 152-8550, JPN) ,  AKASAKA Shuichi (Dep. of Chemistry and Materials Sci., Tokyo Inst. of Technol., 2-12-1-S8-43 Ookayama, Meguro-Ku, Tokyo 152-8550, JPN) ,  ASAI Shigeo (Dep. of Chemistry and Materials Sci., Tokyo Inst. of Technol., 2-12-1-S8-43 Ookayama, Meguro-Ku, Tokyo 152-8550, JPN) ,  SUMITA Masao (Dep. of Chemistry and Materials Sci., Tokyo Inst. of Technol., 2-12-1-S8-43 Ookayama, Meguro-Ku, Tokyo 152-8550, JPN)
資料名： Composites Science and Technology  (Composites Science and Technology)
巻： 70  号： 1  ページ： 200-205  発行年： 2010年01月 
JST資料番号： H0433A  ISSN： 0266-3538  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究はポリ(L-ラクチド)(PLLA)/ポリメタクリル酸メチル(PMMA)/炭素充填材複合材料の電気的性質の変更にポリマ分解性を利用することを試みた。3種類の炭素粒子,すなわちカーボンブラック,気相成長炭素繊維,及びカーボンナノチューブをPLLA/PMMAブレンドと配合し,続いて複合材料の加水分解を行い,試料表面からPLLA分子鎖が分解し,PMMAと炭素粒子については分解することなく残っている結果となった。分解速度を制御することによって,低い表面抵抗率の試料を調製できたが,同時に高い体積抵抗率値を示した。分解複合材料の最終の電気的性質は充填材の寸法と形態によって決まることも分かった。Copyright 2009 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *強化熱可塑性プラスチック ,  *ポリ乳酸 ,  *ポリメタクリル酸メチル ,  *炭素材 ,  微粒子 ,  カーボンブラック ,  炭素繊維 ,  *プラスチックシート ,  圧縮成形 ,  動的機械分析 ,  温度依存性 ,  *加水分解 ,  アルカリ処理 ,  重量損失 ,  表面構造 ,  走査電子顕微鏡 ,  *電気抵抗率 ,  充填材料 ,  形状効果 ,  サイズ効果 ,  体積抵抗率 ,  表面抵抗率 ,  VGCF【繊維】 ,  構造