放電プラズマ焼結によるグリシン-硝酸塩法からの透明イットリア安定化ジルコニア

Transparent yttria stabilized zirconia from glycine-nitrate process by spark plasma sintering

著者 (6件)： LEI Liwen (State Key Lab of Advanced Technol. for Materials Synthesis and Processing, Wuhan Univ. of Technol., Wuhan 430070, CHN) ,  LEI Liwen (School of Materials Sci. and Engineering, Wuhan Univ. of Technol., Wuhan 430070, CHN) ,  FU Zhengyi (State Key Lab of Advanced Technol. for Materials Synthesis and Processing, Wuhan Univ. of Technol., Wuhan 430070, CHN) ,  WANG Hao (State Key Lab of Advanced Technol. for Materials Synthesis and Processing, Wuhan Univ. of Technol., Wuhan 430070, CHN) ,  LEE Soo Wohn (Dep. of Environmental Engineering, Sun Moon Univ., Chungnam 336-708, KOR) ,  NIIHARA Koichi (Extreme Energy-Density Res. Inst., Nagaoka Univ. of Technol., 1603-1 Kamitomioka, Nagaoka, Niigata 940-2188, JPN)
資料名： Ceramics International  (Ceramics International)
巻： 38  号： 1  ページ： 23-28  発行年： 2012年01月 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ナノサイズ立方晶イットリア安定化ジルコニア(ZrO₂-8mol%Y₂O₃)粉末を高エネルギーボールミルミリングと組合せたグリシン-硝酸塩法により合成した。粉末の焼結活性に及ぼすか焼温度の影響を調べた。本稿では,焼結性が高い微細ナノ粉末を得るための最適なか焼温度は900°Cであることを示した。ナノ粉末の固化は,1200~1350°C,5分間の放電プラズマ焼結により行った。1300°Cで透明セラミックスが得られた。Mie理論に基づく光透過率の計算は,1300°Cで焼結した透明試料の実験結果と良好なあてはめを示した。1350°Cで焼結した試料の600nm以上における不一致は,結晶粒界と高い酸素空孔の含有量による散乱に起因すると思われた。Copyright 2011 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *セラミック ,  酸化イットリウム ,  酸化ジルコニウム ,  長さ ,  透明材料 ,  *焼結 ,  焼結性 ,  放電焼結 ,  硝酸塩 ,  粉砕 ,  ボールミル ,  か焼 ,  温度 ,  微細構造 ,  緻密化 ,  相対密度 ,  透過率 ,  理論 ,  結晶粒界 ,  空格子点 ,  結晶度 ,  アミノ酸 ,  脂肪族アミン ,  脂肪族カルボン酸 ,  放電プラズマ焼結
準シソーラス用語： Mie理論 ,  イットリア安定化ジルコニア ,  か焼温度 ,  ナノサイズ ,  メカニカルミリング ,  光透過率 ,  酸素空孔 ,  微細組織