エチレンの酸化ニッケル接触低温酸化脱水素反応でのNbの影響

Nb effect in the nickel oxide-catalyzed low-temperature oxidative dehydrogenation of ethane

著者 (7件)： ZHU Haibo (KAUST Catalysis Center, 4700 King Abdullah Univ. of Sci. and Technol., Thuwal 23955-6900, Saudi Arabia) ,  OULD-CHIKH Samy (KAUST Catalysis Center, 4700 King Abdullah Univ. of Sci. and Technol., Thuwal 23955-6900, Saudi Arabia) ,  ANJUM Dalaver H. (FEI Co., 5350 NE Dawson Creek Drive, Hillsboro, OR 97124, USA) ,  SUN Miao (KAUST Catalysis Center, 4700 King Abdullah Univ. of Sci. and Technol., Thuwal 23955-6900, Saudi Arabia) ,  BIAUSQUE Gregory (KAUST Catalysis Center, 4700 King Abdullah Univ. of Sci. and Technol., Thuwal 23955-6900, Saudi Arabia) ,  BASSET Jean-marie (KAUST Catalysis Center, 4700 King Abdullah Univ. of Sci. and Technol., Thuwal 23955-6900, Saudi Arabia) ,  CAPS Valerie (KAUST Catalysis Center, 4700 King Abdullah Univ. of Sci. and Technol., Thuwal 23955-6900, Saudi Arabia)
資料名： Journal of Catalysis  (Journal of Catalysis)
巻： 285  号： 1  ページ： 292-303  発行年： 2012年01月 
JST資料番号： H0480A  ISSN： 0021-9517  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： クエン酸中で得られたニッケルリッチNb-Niゲルの緩やかな酸化によるNiO及びNb-NiOナノ複合材の合成方法を開発した。得られたものは,従来の硝酸ニッケル及びしゅう酸ニオブアンモニウム塩からの蒸着法に比べて,表面積が高いことが分かった。これらはNiNB₂O₆に似た構造を持ったニオブリッチ混合酸化物の非晶質薄膜(1-2nm)を持ち,Nb含量が>3%で会合したNiOナノ結晶(7-13nm)からなることが分かった。塊状酸化ニッケルとは違って,低温エチレン酸化脱水素(ODH)のためのこれらのナノ酸化物の活性はそれらのレドックス性と関連があることが分かった。Copyright 2011 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *酸化的脱水素 ,  酸化ニッケル ,  ニオブ化合物 ,  添加物効果 ,  非晶質 ,  薄膜 ,  酸化還元反応 ,  表面積 ,  触媒活性 ,  *ニッケル触媒 ,  アルケン ,  脂肪族アルコール ,  脂肪族カルボン酸 ,  ヒドロキシ酸 ,  ポリカルボン酸

分類 (3件)： 反応操作(単位反応)  (XE01040I) ,  酸化,還元  (CF02060T) ,  コバルトとニッケルの錯体  (CE01092Y)

物質索引 (2件)： エチレン ,  クエン酸

タイトルに関連する用語 (5件)： エチレン ,  酸化ニッケル ,  低温酸化 ,  脱水素反応 ,  Nb