ポリ(D,L-乳酸)/ポリ(オキシエチレン)ブレンド中のポリ(オキシエチレン)の高次結晶構造

Higher-order crystalline structures of poly(oxyethylene) in poly(d,l-lactide)/poly(oxyethylene) blends

著者 (9件)： TIEN Nguyen-dung (Dep. of Biobased Materials Sci., Kyoto Inst. of Technol., Matsugasaki, Sakyo-ku, Kyoto 606-8585, JPN) ,  HOA Ta-phuong (Polymer Centre, Hanoi Univ. of Sci. and Technol., Viet Nam) ,  MOCHIZUKI Masatsugu (Center for Fiber and Textile Sci., Kyoto Inst. of Technol., JPN) ,  SAIJO Kenji (Dep. of Polymer Chemistry, Kyoto Univ., JPN) ,  HASEGAWA Hirokazu (Dep. of Polymer Chemistry, Kyoto Univ., JPN) ,  SASAKI Sono (Dep. of Biobased Materials Sci., Kyoto Inst. of Technol., Matsugasaki, Sakyo-ku, Kyoto 606-8585, JPN) ,  SASAKI Sono (Center for Fiber and Textile Sci., Kyoto Inst. of Technol., JPN) ,  SAKURAI Shinichi (Dep. of Biobased Materials Sci., Kyoto Inst. of Technol., Matsugasaki, Sakyo-ku, Kyoto 606-8585, JPN) ,  SAKURAI Shinichi (Center for Fiber and Textile Sci., Kyoto Inst. of Technol., JPN)
資料名： Polymer  (Polymer)
巻： 54  号： 17  ページ： 4653-4659  発行年： 2013年08月02日 
JST資料番号： D0472B  ISSN： 0032-3861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 小角X線散乱(SAXS)を用いて,ポリ乳酸/ポリ(オキシエチレン)(PLA/PEG)における高次結晶構造を研究した。この目的に対し,2つブレンドの高分子が結晶性の両方であるという事実は状況を非常に複雑にする。簡単にするために,D-およびL-乳酸部分を含むラセミ共重合体である非結晶性PLA,ポリ(D,L-乳酸)(DLPLA)を使用した。ジクロロメタン中の溶液からキャスティングしたPEG100%の試料並びに種々のブレンド試料で,PEGの秩序化ラメラスタッキング(すなわち格子ピーク)から生じる高次ピークを観測した。驚くべきことに,PEG100%試料と比べ,DLPLAの5~20wt%の組成でDLPLA/PEGブレンドでは,その構造が多かれ少なかれ規則的であることを見出した。さらに,温度による正規構造の変化を検討し,ラメラ粒子散乱に帰することができる1°Cの溶融温度以下の非常に独特なSAXSプロファイルを見出した。Copyright 2013 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ポリ乳酸 ,  *高次構造 ,  結晶構造 ,  *ポリエチレンオキシド ,  *ポリマブレンド ,  小角X線散乱 ,  示差走査熱量測定 ,  ラセミ体
準シソーラス用語： SAXS【散乱】

分類 (1件)： 高分子固体の構造と形態学  (CG02022M)

タイトルに関連する用語 (4件)： L-乳酸 ,  オキシエチレン ,  ブレンド ,  結晶構造