Fe-Ni系合金中のγ′′-Ni₃Nb析出物

γ′′-Ni₃Nb precipitate in Fe-Ni base alloy

著者 (7件)： SANO Keisuke (Hokkaido Univ., Graduate School of Engineering, Materials Sci. and Engineering: N13, W-8, Kita-ku, Sapporo 060-8628, JPN) ,  OONO Naoko (Hokkaido Univ., Fac. of Engineering, Materials Sci. and Engineering: N13, W-8, Kita-ku, Sapporo 060-8628, JPN) ,  UKAI Shigeharu (Hokkaido Univ., Fac. of Engineering, Materials Sci. and Engineering: N13, W-8, Kita-ku, Sapporo 060-8628, JPN) ,  HAYASHI Shigenari (Hokkaido Univ., Fac. of Engineering, Materials Sci. and Engineering: N13, W-8, Kita-ku, Sapporo 060-8628, JPN) ,  INOUE Toshihiko (Advanced Nuclear System R&D Directorate, Japan Atomic Energy Agency (JAEA): 4002, Narita, Oarai, Ibaraki-pref ...) ,  YAMASHITA Shinichiro (Advanced Nuclear System R&D Directorate, Japan Atomic Energy Agency (JAEA): 4002, Narita, Oarai, Ibaraki-pref ...) ,  YOSHITAKE Tsunemitsu (Advanced Nuclear System R&D Directorate, Japan Atomic Energy Agency (JAEA): 4002, Narita, Oarai, Ibaraki-pref ...)
資料名： Journal of Nuclear Materials  (Journal of Nuclear Materials)
巻： 442  号： 1-3  ページ： 389-393  発行年： 2013年11月 
JST資料番号： D0148A  ISSN： 0022-3115  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 標準の化学組成Fe-43Ni-15Cr-2W-1Mo-3.8Nb-0.1V-0.1Ti-0.28Al-0.1Zr-0.04C(質量%)中の準安定γ′′-Ni₃Nb析出物が関与するFe-Ni合金に対して,20%冷間圧延後,温度650~750°Cにおいて200時間までの時効処理時の硬度測定とTEM分析を行った。コヒーレントγ′′-Ni₃Nb析出物故に硬度が上昇したが,時効処理が延びるとその粗大化と転位回復により硬度が低下した。800°C,200時間の時効処理では,安定したδ-Ni₃Nbへ変態した。これらのデータに基づいて,製造の最終段階で結晶粒内γ′′析出物を微細に分布させるために適する時効処理条件として700-750°C,8時間を考えた。Copyright 2013 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *鉄合金 ,  ニオブ化合物 ,  ニッケル化合物 ,  ニッケル含有合金 ,  クロム含有合金 ,  ニオブ含有合金 ,  アルミニウム含有合金 ,  時効処理 ,  硬度 ,  電子顕微鏡観察 ,  温度依存性 ,  *析出物 ,  *原子炉材料

分類 (1件)： 原子炉の構成要素と原子炉材料一般  (MD04010I)

タイトルに関連する用語 (2件)： Fe-Ni系合金 ,  析出物