異なる方法で調製したヒドロキシアパタイト粉末の焼結特性

Sintering properties of hydroxyapatite powders prepared using different methods

著者 (9件)： RAMESH S. (Ceramics Technol. Lab., 43009 Kajang, Selangor, Malaysia) ,  AW K.l. (Fac. of Sci. and Engineering, Laval Univ., Quebec, Canada G1V 0A6) ,  TOLOUEI R. (Ceramics Technol. Group, SIRIM Berhad, 1 Persiaran Dato Menteri, Shah Alam, Malaysia) ,  AMIRIYAN M. (Ceramics Technol. Group, SIRIM Berhad, 1 Persiaran Dato Menteri, Shah Alam, Malaysia) ,  TAN C.y. (Fac. of Sci. and Engineering, Laval Univ., Quebec, Canada G1V 0A6) ,  HAMDI M. (Ceramics Technol. Lab., 43009 Kajang, Selangor, Malaysia) ,  PURBOLAKSONO J. (Dep. of Engineering Design and Manufacturing, Advanced Manufacturing and Material Processing (AMMP) Centre, Univ. of ...) ,  HASSAN M.a. (Dep. of Engineering Design and Manufacturing, Advanced Manufacturing and Material Processing (AMMP) Centre, Univ. of ...) ,  TENG W.d. (Ceramics Technol. Group, SIRIM Berhad, 1 Persiaran Dato Menteri, Shah Alam, Malaysia)
資料名： Ceramics International  (Ceramics International)
巻： 39  号： 1  ページ： 111-119  発行年： 2013年01月 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,湿式析出法(HAp)及び湿式メカノケミカル法(HAwm)により調製したHA粒子の焼結挙動を調べた。また比較の目的で商用HA粉末(HAc)の焼結挙動を研究した。3つのすべての粉末を,粒子サイズ,Ca/P比及び結晶サイズにより特性付けた。成形試料を調製し,1000から1400°Cの温度範囲の空気中で焼結した。焼結体の相安定性,相対密度,ヤング率,ビッカース硬度,破壊靭性及び粒径を調べた。その結果は,HAwm試料が相分解を受けたのに対して,HAp及びHAc試料は,採用したすべての温度に渡って相分解を示さなかった。HAp試料はHAc及びHAwm試料と比較した場合,全体的に最も良好な緻密性と特性を示した。さらにその結果は,焼結試料の機械的性質がバルク密度と粒径に支配されることを示した。Copyright 2013 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ヒドロキシアパタイト ,  微粉体 ,  *焼結性 ,  焼結 ,  メカノ化学 ,  析出 ,  湿式法 ,  結晶粒径 ,  焼結体 ,  相安定性 ,  相対密度 ,  Young率 ,  押込硬さ ,  破壊靱性 ,  相分離 ,  緻密化 ,  *機械的性質 ,  *燐灰石

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (4件)： 調製 ,  ヒドロキシアパタイト ,  粉末 ,  焼結特性