急冷凝固粉末から作製したBi-Sb-Teバルク材料の微細構造と熱電特性【Powered by NICT】

Microstructure and thermoelectric properties of Bi-Sb-Te bulk materials fabricated from rapidly solidified powders

著者 (4件)： Wang Zhi-Lei (Department of Mechanical and Aerospace Engineering, Graduate School of Engineering, Tottori University, Koyama-minami 4-101, Tottori 680-8552, Japan) ,  Akao Takahiro (Department of Mechanical Engineering, National Institute of Technology, Fukushima College, Nagao 30, Taira Kamiarakawa, Iwaki 970-8034, Japan) ,  Onda Tetsuhiko (Department of Mechanical and Aerospace Engineering, Graduate School of Engineering, Tottori University, Koyama-minami 4-101, Tottori 680-8552, Japan) ,  Chen Zhong-Chun (Department of Mechanical and Aerospace Engineering, Graduate School of Engineering, Tottori University, Koyama-minami 4-101, Tottori 680-8552, Japan)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 136  ページ： 111-114  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 急速凝固と放電プラズマ焼結技術はBi-Sb-Teバルク熱電材料を作製した。焼結試料中の粒界は主に大傾角粒界から構成されていたが,大部分小傾角粒界の高い焼結温度であることが分かった。焼結温度が増加すると,Seebeck係数はほとんど変化しなかったが,電気抵抗率は徐々に減少した。熱伝導率は420°Cまで増加し緩やかに,その後急激に増加した。結果として,1.1の最大ZT値は400°Cで焼結した試料,メカニカルアロイングした粉末から調製したものと比較して44.7%増加するで達成された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *急冷凝固 ,  メカニカルアロイング ,  結晶粒界 ,  放電プラズマ焼結 ,  *粉体 ,  高傾角粒界 ,  電気抵抗率 ,  熱電材料 ,  小傾角粒界 ,  熱伝導率 ,  焼結 ,  Seebeck係数 ,  焼結温度 ,  *急冷凝固粉 ,  改変
準シソーラス用語： *熱電特性 , 【Automatic Indexing@JST】

著者キーワード (5件)： テルル化ビスマス ,  Microstructure ,  熱電材料 ,  急冷凝固 ,  スパークプラズマ焼結

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (8件)： 急冷凝固粉 ,  作製 ,  BI ,  Sb ,  Te ,  バルク材料 ,  微細構造 ,  熱電特性