液体処理における酸化グラフェンのサイズ減少を制御する構造因子【Powered by NICT】

Structural factors controlling size reduction of graphene oxide in liquid processing

著者 (16件)： Nacken Thomas J. (Institute of Particle Technology (LFG), Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Cauerstrasse 4, 91058 Erlangen, Germany) ,  Halbig Christian E. (Institute for Chemistry and Biochemistry, Freie Universitaet Berlin, Takustrasse 3, 14195, Berlin, Germany) ,  Halbig Christian E. (Institute of Advanced Materials and Processes (ZMP), Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Dr.-Mack Str. 81, 90762, Fuerth, Germany) ,  Wawra Simon E. (Institute of Particle Technology (LFG), Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Cauerstrasse 4, 91058 Erlangen, Germany) ,  Damm Cornelia (Institute of Particle Technology (LFG), Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Cauerstrasse 4, 91058 Erlangen, Germany) ,  Romeis Stefan (Institute of Particle Technology (LFG), Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Cauerstrasse 4, 91058 Erlangen, Germany) ,  Walter Johannes (Institute of Particle Technology (LFG), Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Cauerstrasse 4, 91058 Erlangen, Germany) ,  Walter Johannes (Interdisciplinary Center for Functional Particle Systems (FPS), Friedrich-Alexander Universitaet Erlangen-Nuernberg (FAU), Haberstrasse 9a, 91058 Erlangen, Germany) ,  Tehrani Mohammad J. (Department of Chemistry, University of Illinois at Chicago, 845 W Taylor St, Chicago, IL 60607, USA) ,  Hu Yichen (Department of Chemistry, University of Illinois at Chicago, 845 W Taylor St, Chicago, IL 60607, USA) ,  Ishii Yoshitaka (Department of Chemistry, University of Illinois at Chicago, 845 W Taylor St, Chicago, IL 60607, USA) ,  Ishii Yoshitaka (School of Life Science and Technology, Tokyo Institute of Technology, Nagatsuda 4259, Midori-ku, Yokohama 226-8503 Japan) ,  Eigler Siegfried (Institute for Chemistry and Biochemistry, Freie Universitaet Berlin, Takustrasse 3, 14195, Berlin, Germany) ,  Eigler Siegfried (Institute of Advanced Materials and Processes (ZMP), Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Dr.-Mack Str. 81, 90762, Fuerth, Germany) ,  Peukert Wolfgang (Institute of Particle Technology (LFG), Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Cauerstrasse 4, 91058 Erlangen, Germany) ,  Peukert Wolfgang (Interdisciplinary Center for Functional Particle Systems (FPS), Friedrich-Alexander Universitaet Erlangen-Nuernberg (FAU), Haberstrasse 9a, 91058 Erlangen, Germany)
資料名： Carbon  (Carbon)
巻： 125  ページ： 360-369  発行年： 2017年 
JST資料番号： H0270B  ISSN： 0008-6223  CODEN： CRBNA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： グラフェン酸化物材料は多様体合成法で調製でき,所望の特性を採用するさらに後官能化を可能にした。100nmスケールの横方向の大きさが小型シートは,例えば電池応用のための有益である。液相処理によるシートの破壊は,このようなナノサイズのシートを生成するために理想的な方法である。しかし,今までのところ,それは官能化は,破壊挙動にどのように影響するかは知られていない。<1%グラフェンシートの官能化のタイプと程度に関してフレークの超音波処理へのサイズ減少速度を評価するために格子欠陥を持つ単層オキソ官能化グラフェン(オキソG)誘導体を選択した。加工シートの横方向寸法は分析用超遠心により溶液中で定量的に決定した。最高サイズ減少速度は,元のオキソGで観察され,それは約60%の官能化と負に帯電した硫酸基の最高度を持っていた。有機硫酸塩の部分的加水分解,または大部分または部分的脱官能基のヒドロキシル基への表面官能基の転化率は初期オキソGと比較して25%まで低いサイズ縮小速度をもたらした。さらに,サイズ減少速度を紫外可視分光法でも第一近似で相関させることができる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： フレーク ,  ヒドロキシ基 ,  官能化 ,  近似法 ,  硫酸塩 ,  *構造因子 ,  転化率 ,  加水分解 ,  *グラフェン ,  格子欠陥 ,  液相 ,  単一層
準シソーラス用語： 紫外可視分光法 ,  官能基 ,  *酸化グラフェン , 【Automatic Indexing@JST】

分類 (1件)： 炭素とその化合物  (YB02060D)

タイトルに関連する用語 (4件)： 液体処理 ,  酸化グラフェン ,  サイズ ,  構造因子