スーパーキャパシタ用のNi発泡体上に形成されたNiCo_2O_4とNiCo_2S_4の性能比較【Powered by NICT】

Performance comparison of NiCo₂O₄ and NiCo₂S₄ formed on Ni foam for supercapacitor

著者 (5件)： Jinlong Lv (Fracture and Reliability Research Institute, School of Engineering, Tohoku University, Sendai 9808579, Japan) ,  Tongxiang Liang (School of Materials Science and Engineering, Jiangxi University of Science and Technology, Ganzhou, China) ,  Meng Yang (Fracture and Reliability Research Institute, School of Engineering, Tohoku University, Sendai 9808579, Japan) ,  Ken Suzuki (Fracture and Reliability Research Institute, School of Engineering, Tohoku University, Sendai 9808579, Japan) ,  Hideo Miura (Fracture and Reliability Research Institute, School of Engineering, Tohoku University, Sendai 9808579, Japan)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 123  ページ： 28-33  発行年： 2017年 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Ni発泡体上に整列したNiCo_2S_4ナノチューブを水熱法により合成したNiCo前駆体の完全な硫化によって得た。Ni発泡体上にNiCo_2S_4ナノチューブをNi発泡体上にNiCo_2O_4ナノワイヤよりも高い比静電容量を示した。Ni発泡体上にNiCo_2S_4ナノチューブは1Ag~( 1)で1936.2Fg~( 1)の高い静電容量を示した。Ni発泡体上に多孔質NiCo_2S_4ナノチューブは電気化学反応のための露出した活性部位の膨大な数を提供した。さらに,大きな比表面積を持つNi発泡体上にNiCo_2S_4ナノチューブは電解質と改善された電気化学的反応の拡散および浸透を促進した。,5000回の連続充放電サイクル後,比静電容量のわずか約7.9%の分解がNi発泡体上にNiCo_2S_4ナノチューブで観察された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 電解質 ,  ナノワイヤ ,  電気化学反応 ,  充放電サイクル ,  活性部位 ,  水熱合成 ,  静電容量 ,  *ニッケル ,  比表面積 ,  前駆体 ,  多孔性
準シソーラス用語： 比静電容量 ,  *性能比較 ,  *発泡体 ,  *スーパーキャパシタ , 【Automatic Indexing@JST】

著者キーワード (4件)： NiCo_2S_4 ,  水熱プロセス ,  スーパーキャパシタ ,  Microstructures

分類 (2件)： 強化プラスチックの成形  (YH04060J) ,  静電機器  (NB10020R)

タイトルに関連する用語 (4件)： スーパーキャパシタ ,  Ni ,  発泡体 ,  性能比較