無電解析出によりNi修飾したAl₂O₃粉末の作製に関するイオン液体添加物[bmim]BF₄の効果

Effects of ionic liquid additive [bmim]BF₄ on fabrication of Ni-decorated Al₂O₃ powders by electroless deposition

著者 (6件)： Ru Juanjian (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, PR China) ,  Feng Jing (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, PR China) ,  Jiang Yehua (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, PR China) ,  Zhou Rong (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, PR China) ,  Hua Yixin (Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming 650093, PR China) ,  Hua Yixin (State Key Lab of Complex Nonferrous Metal Resources Clean Utilization, Kunming 650093, PR China)
資料名： Advanced Powder Technology  (Advanced Powder Technology)
巻： 28  号： 2  ページ： 430-437  発行年： 2017年02月 
JST資料番号： W0255A  ISSN： 0921-8831  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 添加物として25g/Lの[bmim]BF₄イオン液体を含む硫酸塩溶液からの無電解析出により,Al₂O₃粉末上に連続かつ均一なNi被覆層を作製した。Ni修飾したAl₂O₃粉末の表面形態,被覆厚,元素分布に関する[bmim]BF₄濃度の影響を検討した。0~35g/L範囲で[bmim]BF₄濃度の増加に伴い,Al₂O₃表面から離れて分離したNi粉末とクラスターの生成が減少した。これは,Al₂O₃表面も突起と鋭部に[bmim]BF₄添加物の選択吸着により,迅速な核化とNiの結晶成長が抑制され,よって,均一なNi修飾のAl₂O₃粉末が得られたと説明できた。[bmim]BF₄濃度が25g/Lのとき,Al₂O₃表面のNi粒子が均一で,0.5~1.5μmの平均サイズで被覆厚は約2.0~3.0μmの回転楕円体となった。その上,Ni被覆層の析出の結果を異なる反応段階から得られた被覆生成物の形態変化に従って分析した。さらに,添加物として[bmim]BF₄を伴うNi修飾したAl₂O₃粉末の析出過程の経験的モデルを提案して,被覆層構造の生成メカニズムをさらに詳しく述べた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 酸化アルミニウム ,  *無電解めっき ,  ニッケルめっき ,  イオン液体 ,  添加物効果
準シソーラス用語： *無電解析出 ,  無電解ニッケルめっき

著者キーワード (5件)： Ni-decorated Al₂O₃ ,  Electroless deposition ,  Ionic liquid ,  Additive ,  Deposition mechanism

分類 (1件)： 無電解めっき  (WC08024S)

引用文献 (28件)：

• M. Uysal, R. Karslioğlu, A. Alp, H. Akbulut, The preparation of core-shell Al₂O₃/ Ni composite powders by electroless plating, Ceram. Int 39 (2013) 5485-5493.
• H. Beygi, S.A. Saijadi, S.M. Zebarjad, An optimization analysis on electroless deposition of Al₂O₃/Cu core-shell nanostructures, Appl. Surf. Sci. 261 (2012) 166-173.
• H. Wang, J. Jia, H. Song, X. Hu, H. Sun, D. Yang, The preparation of Cu-coated Al₂O₃ composite powders by electroless plating, Ceram. Int. 37 (2011) 2181- 2184.
• L Esposito, A. Bellosi, S. Guicciardi, G. De Portu, Solid state bonding of Al₂O₃ with Cu, Ni and Fe: characteristics and properties, J. Mater. Sci. 33 (1998) 1827-1836.
• X.J. Wei, J.T. Liang, L Zhen, Y.X. Gong, W.Z. Shao, C.V. Xu, Synthesis of Fe/SiO₂ composite particles and their superior electromagnetic properties in microwave band, Mater. Lett. 64 (2010) 57-60.

タイトルに関連する用語 (9件)： 無電解析出 ,  Ni ,  修飾 ,  Al2O3 ,  粉末 ,  作製 ,  イオン液体 ,  添加物 ,  BMIM