Yb B系におけるほう素リッチ相について【Powered by NICT】

On the boron rich phases in the Yb-B system

著者 (8件)： Sologub Oksana (Institute of Solid State Physics, TU Wien, A-1040 Vienna, Austria) ,  Salamakha Leonid P. (Institute of Solid State Physics, TU Wien, A-1040 Vienna, Austria) ,  Stoger Berthold (X-Ray Centre, TU Wien, A-1060 Vienna, Austria) ,  Rogl Peter F. (Institute of Materials Chemistry and Research, University of Vienna, A-1090 Vienna, Austria) ,  Mori Takao (National Institute for Materials Science, MANA, Namiki 1-1, Tsukuba 305-0044, Japan) ,  Eguchi Gaku (Institute of Solid State Physics, TU Wien, A-1040 Vienna, Austria) ,  Michor Herwig (Institute of Solid State Physics, TU Wien, A-1040 Vienna, Austria) ,  Bauer Ernst (Institute of Solid State Physics, TU Wien, A-1040 Vienna, Austria)
資料名： Journal of Solid State Chemistry  (Journal of Solid State Chemistry)
巻： 255  ページ： 172-177  発行年： 2017年 
JST資料番号： H0505A  ISSN： 0022-4596  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 二ほう素リッチ相は真空下でのYb酸化物のホウ素熱還元によって合成することに成功した。新しいホウ素貧弱相では,単相は約1500°Cでの[B]/[Yb]=43.3(Pbam空間群;YB_50型,=16.5811(5)Å,17.5950(5)Å,9.4647(3)Å,粉末X線回折,Rietveld精密化)で確立した。ほう素豊富相([B]/[Yb]=56.7)の結晶構造を単結晶X線回折(3m c空間群;YB_66型,=23.3587(6)Å)により明らかにした。1825°Cで焼鈍した合金YbB_~70の粉末X線回折データは,YB_66型化合物(=23.3691(2)Å)に加えて,二次相(R3 m空間群=10.9298(3)Å,=23.875(1)Å)としてβ-rh B,Ybの溶解度は1で%以下であることが分かったが得られた。β-rh B中のYb原子はDおよびEボイドを占有した。YbB_43(YB_50型)とYbB_56(YB_66型)の両方は,プロトタイプ構造で観察されたものと比べて内およびほう素クラスタ間で短いB-B分離を示す複雑なホウ素原子骨格を特徴とする。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *ホウ素 ,  X線回折 ,  合金 ,  クラスタ ,  精密化 ,  *イッテルビウム ,  第二相 ,  単相 ,  ホウ化物 ,  結晶構造 ,  酸化物 ,  溶解度 ,  空間群
準シソーラス用語： 単結晶X線回折 ,  粉末X線回折 , 【Automatic Indexing@JST】

著者キーワード (4件)： 希土類ほう化物 ,  ほう素二十面体フレームワーク ,  結晶構造 ,  X線回折