10J/cm2以上の高レーザエネルギー密度のPLDを用いた種々の基板上のNd-Fe-B/α-Feナノ複合厚膜磁石の作製【JST・京大機械翻訳】

Preparation of Nd-Fe-B/α-Fe nano-composite thick-film magnets on various substrates using PLD with high laser energy density above 10 J/cm²

著者 (6件)： Nakano M. (Graduate School of Engineering, Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Kondo H. (Graduate School of Engineering, Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Yamashita A. (Graduate School of Engineering, Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Yanai T. (Graduate School of Engineering, Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Itakura M. (Interdisciplinary Graduate School of Engineering Sciences, Kyushu University, 6-1 Kasuga-kouen, Kasuga 816-8580, Japan) ,  Fukunaga H. (Graduate School of Engineering, Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 8  号： 5  ページ： 056223-056223-6  発行年： 2018年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 10J/cm2以上の高レーザエネルギー密度(LED)を有するPLD(パルス化レーザ蒸着)法とそれに続くフラッシュアニーリングにより,多結晶Ta基板上に(BH)_max≧80kJ/m3の等方性ナノ複合材料厚膜磁石を得ることができた。また,平均粒径が約20nmのNd_2Fe_14B相と共にα-Feから成る分散構造がTa基板上に形成されることを実証した。本研究では,Ti,NbおよびWのような各高融点を有する異なる金属ベース基板の使用により,微細構造を制御することにより(BH)_max値を強化することを試みた。基板上に堆積した膜の微細構造を変化させ,磁気特性を改善することは困難であったが,ナノ分散α-FeとNd_2Fe_14B相に基づく(BH)_max≧80kJ/m3の等方性厚膜磁石が,種々の金属基板上に完全に異なる多結晶構造をもつことを確認した。一方,ガラス基板の使用は,同じ調製プロセスを用いて調製した膜の磁気特性の劣化をもたらす。(翻訳著者抄録)【JST・京大機械翻訳】

シソーラス用語： 等方性 ,  レーザ蒸着 ,  多結晶 ,  タンタル ,  *レーザ ,  *ナノ複合材料 ,  パルス化 ,  磁気的性質 ,  *エネルギー密度 ,  微細構造
準シソーラス用語： ガラス基板 ,  金属基板 ,  ナノ分散 ,  平均粒子径 ,  *厚膜磁石 , 【Automatic Indexing@JST】

分類 (2件)： 電磁石  (NA05080G) ,  磁性材料  (NA04040H)

タイトルに関連する用語 (8件)： レーザ ,  エネルギー密度 ,  PLD ,  Nd ,  Fe ,  ナノ複合 ,  厚膜磁石 ,  作製