27TにおけるパウダーインチューブBa_0.6K_0.4Fe₂As₂テープの高輸送電流超伝導

High transport current superconductivity in powder-in-tube Ba_0.6K_0.4Fe₂As₂ tapes at 27T

著者 (10件)： HUANG He (Inst. Electrical Engineering, Chinese Acad. Sci., Beijing, CHN) ,  YAO Chao (Inst. Electrical Engineering, Chinese Acad. Sci., Beijing, CHN) ,  DONG Chiheng (Inst. Electrical Engineering, Chinese Acad. Sci., Beijing, CHN) ,  ZHANG Xianping (Inst. Electrical Engineering, Chinese Acad. Sci., Beijing, CHN) ,  WANG Dongliang (Inst. Electrical Engineering, Chinese Acad. Sci., Beijing, CHN) ,  CHENG Zhe (Inst. Electrical Engineering, Chinese Acad. Sci., Beijing, CHN) ,  LI Jianqi (Inst. Physics, Chinese Acad. Sci., Beijing, CHN) ,  AWAJI Satoshi (Tohoku Univ., Sendai, JPN) ,  WEN Haihu (Nanjing Univ., Nanjing, CHN) ,  MA Yanwei (Inst. Electrical Engineering, Chinese Acad. Sci., Beijing, CHN)
資料名： 東北大学金属材料研究所強磁場超伝導材料研究センター年次報告  (Annual Report. High Field Laboratory for Superconducting Materials, Institute for Materials Research, Tohoku University)
巻： 2017  ページ： 10-13  発行年： 2018年06月 
JST資料番号： X0986A  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： 日本 (JPN)  言語： 英語 (EN)

抄録/ポイント： ・多様な分野の利用に有力な候補である鉄系超電導体を中心に研究を実施。
・本研究では,初めて最適化しホットプレス法により高性能な超電導線テープBa-122(Ba_0.6K_0.4Fe₂As₂)の製造に成功。
・Ba-122の前駆体を固相反応法で調製し,Sn(5%)を添加剤しPIT法とホットプレスプロセスによりテープを製造。
・輸送Jc値は従来の鉄系超伝導線およびテープの最高で10Tで5.5×10⁵A/cm²(Ic=437A),27Tで5.5×10⁴A/cm²。
・Ba-122テープはc軸配向度が高く,9°以内に多数の結晶粒界が見られるのが特徴。

シソーラス用語： 臨界電流密度 ,  最適化 ,  *ホットプレス ,  超伝導線 ,  固相反応 ,  磁気的性質 ,  添加剤 ,  *鉄系超伝導体 ,  *線引 ,  *電流 ,  超伝導
準シソーラス用語： *PIT法 ,  *輸送電流

分類 (1件)： 金属系超伝導体の物性  (BM04022R)

引用文献 (15件)：

• Kamihara Y, et al., J. Am. Chem. Soc. 130 3296 (2008)
• Rotter M, et al., Phys. Rev. Lett. 101 107006 (2008)
• Gurevich A, Nat. Mater. 10 255 (2011)
• Yamamoto A, et al., Appl. Phys. Lett. 92 252501 (2008)
• Katase T, et al., Nat. Commun. 2 409 (2011)

タイトルに関連する用語 (3件)： テープ ,  輸送電流 ,  超伝導