太陽水分解のための改質Siナノワイヤ/グラファイト様窒化炭素コア-シェル光アノード【JST・京大機械翻訳】

Modified Si nanowire/graphite-like carbon nitride core-shell photoanodes for solar water splitting

著者 (23件)： Ning Minghui (Guangdong Provincial Key Laboratory of Optical Information Materials and Technology & Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Ning Minghui (National Center for International Research on Green Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Chen Zhen (Guangdong Provincial Key Laboratory of Optical Information Materials and Technology & Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Chen Zhen (National Center for International Research on Green Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Li Lin (Guangdong Provincial Key Laboratory of Optical Information Materials and Technology & Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Li Lin (National Center for International Research on Green Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Meng Qingguo (Shenyang Institute of Automation, Chinese Academy of Sciences, Guangzhou, 511458, PR China) ,  Chen Zhihong (Shenyang Institute of Automation, Chinese Academy of Sciences, Guangzhou, 511458, PR China) ,  Chen Zhihong (International Academy of Optoelectronics at Zhaoqing, South China Normal University, Guangdong Province, PR China) ,  Zhang Yongguang (International Academy of Optoelectronics at Zhaoqing, South China Normal University, Guangdong Province, PR China) ,  Jin Mingliang (Guangdong Provincial Key Laboratory of Optical Information Materials and Technology & Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Jin Mingliang (National Center for International Research on Green Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Jin Mingliang (International Academy of Optoelectronics at Zhaoqing, South China Normal University, Guangdong Province, PR China) ,  Zhang Zhang (Guangdong Provincial Key Laboratory of Optical Information Materials and Technology & Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Zhang Zhang (National Center for International Research on Green Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Zhang Zhang (International Academy of Optoelectronics at Zhaoqing, South China Normal University, Guangdong Province, PR China) ,  Yuan Mingzhe (Shenyang Institute of Automation, Chinese Academy of Sciences, Guangzhou, 511458, PR China) ,  Wang Xin (Guangdong Provincial Key Laboratory of Optical Information Materials and Technology & Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Wang Xin (National Center for International Research on Green Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Wang Xin (International Academy of Optoelectronics at Zhaoqing, South China Normal University, Guangdong Province, PR China) ,  Zhou Guofu (Guangdong Provincial Key Laboratory of Optical Information Materials and Technology & Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Zhou Guofu (National Center for International Research on Green Optoelectronics, South China Normal University, Guangzhou 510006, PR China) ,  Zhou Guofu (International Academy of Optoelectronics at Zhaoqing, South China Normal University, Guangdong Province, PR China)
資料名： Electrochemistry Communications  (Electrochemistry Communications)
巻： 87  ページ： 13-17  発行年： 2018年 
JST資料番号： W1133A  ISSN： 1388-2481  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Siナノワイヤ(SiNW)とグラファイト様窒化炭素(g-C_3N_4)は,太陽水分解のための非常に有望な材料である。本研究では,金属触媒無電解エッチングによりn型SiNW(n-SiNW)を得た。n-SiNWの光電気化学的性能を改善するために,g-C_3N_4を被覆層(n-SiNW/g-C_3N_4)としてそれらの表面上に堆積した。さらに,g-C_3N_4における活性部位の密度を増加させるために,層堆積の前に前駆体にバルビツール酸(BA)を導入した。n-SiNW/g-C_3N_4光アノードは,裸のn-SiNWと比較して,開始電位の負のシフトを示した。さらに,1.6V対RHEにおける光電流密度の50%の増強が,元のn-SiNW/g-C_3N_4と比較して,BA修飾n-SiNW/g-C_3N_4上で達成された。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 前駆体 ,  活性部位 ,  電流密度 ,  *太陽 ,  *ナノワイヤ ,  被覆層 ,  *コアシェル構造 ,  電位 ,  金属触媒 ,  *グラファイト
準シソーラス用語： 電気化学的性能 ,  無電解エッチング ,  *光アノード ,  *窒化炭素 ,  *水分解 , 【Automatic Indexing@JST】

著者キーワード (5件)： 水分解 ,  Siナノワイヤ ,  黒鉛状窒化炭素 ,  コア/シェルナノ構造 ,  共重合改質

分類 (3件)： 電気化学反応  (CB07050F) ,  電極過程  (CB07040U) ,  静電機器  (NB10020R)

タイトルに関連する用語 (9件)： 太陽 ,  水分解 ,  改質 ,  Si ,  ナノワイヤ ,  グラファイト ,  窒化炭素 ,  コア-シェル ,  光アノード