リチウムグリースにおける新規添加剤としての液体金属ガgalのトライボロジー特性【JST・京大機械翻訳】

Tribological properties of liquid-metal galinstan as novel additive in lithium grease

著者 (6件)： Bai Pengpeng (Department of Mechanical Engineering, State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, PR China) ,  Li Shaowei (Department of Mechanical Engineering, State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, PR China) ,  Tao Dashuai (Department of Mechanical Engineering, State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, PR China) ,  Jia Wenpeng (Department of Mechanical Engineering, State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, PR China) ,  Meng Yonggang (Department of Mechanical Engineering, State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, PR China) ,  Tian Yu (Department of Mechanical Engineering, State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, PR China)
資料名： Tribology International  (Tribology International)
巻： 128  ページ： 181-189  発行年： 2018年 
JST資料番号： E0409B  ISSN： 0301-679X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ガリウム基液体金属(GBLM)を異なる割合でグリースに添加し,機械的撹拌とボールミル粉砕により均質化した。リチウムグリースにおける添加剤としての純粋なGBLM,純粋なグリース及びGBLMのトライボロジー特性を4球試験により調べた。その結果,純GBLMは低荷重下で劣った耐摩耗性を示し,高荷重下でのグリースの潤滑性能は満足できないことを示した。GBLMをグリースに添加した後,後者の極限圧力潤滑能力は効果的に増加したが,低負荷下での耐摩耗性性能は低下しなかった。特定の市販リチウムグリースに対するGBLMの質量比が1:1に達したとき,溶接荷重は10kN以上であり,それはグリースの最大値であった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 溶接 ,  *リチウム ,  撹拌 ,  強制潤滑 ,  均質化 ,  *グリース ,  耐摩耗性 ,  液体金属
準シソーラス用語： 質量比 ,  潤滑性 ,  トライボロジー特性 , 【Automatic Indexing@JST】

著者キーワード (4件)： ガリウム基液体金属 ,  リチウムグリース ,  耐摩耗性 ,  極圧潤滑

分類 (2件)： 潤滑一般  (QB02010S) ,  潤滑法  (QB02020D)

タイトルに関連する用語 (5件)： リチウム ,  グリース ,  添加剤 ,  液体金属 ,  トライボロジー特性