スパークプラズマ焼結(SPS)処理中に生じる酸化物セラミックス中の炭素汚染の分布:II-SPSと負荷温度の影響【Powered by NICT】

Distribution of carbon contamination in oxide ceramics occurring during spark-plasma-sintering (SPS) processing: II - Effect of SPS and loading temperatures

著者 (5件)： Morita Koji (Advanced Ceramics Group, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047, Japan) ,  Kim Byung-Nam (Advanced Ceramics Group, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047, Japan) ,  Yoshida Hidehiro (Advanced Ceramics Group, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047, Japan) ,  Hiraga Keijiro (Advanced Ceramics Group, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047, Japan) ,  Sakka Yoshio (Advanced Ceramics Group, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047, Japan)
資料名： Journal of the European Ceramic Society  (Journal of the European Ceramic Society)
巻： 38  号： 6  ページ： 2596-2604  発行年： 2018年 
JST資料番号： E0801B  ISSN： 0955-2219  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： SPS処理中の炭素汚染は,スピネル,アルミナとジルコニアで検討した。炭素汚染はSPS条件とターゲット材料と共に変化した。100°C/minの高い加熱速度では,汚染はスピネル中の全領域にわたって,がアルミナとジルコニアの表面積付近だけで生じた。スピネルの場合,汚染したSPSパラメータ,加熱速度および負荷条件などに敏感であるが,焼結温度に対する感受性が低かった。これは炭素汚染はカーボン紙/金型からのCOガスの蒸発により生じたことを示唆した。高加熱速度では,炭素蒸発は急速加熱により増強されると,蒸着したCOガスは加熱プロセス中閉じた細孔にカプセル化し,マトリクス中に残っている。炭素汚染は,高い加熱速度でも高い温度負荷により抑制することができた。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： アルミナ ,  表面積 ,  酸化ジルコニウム ,  細孔 ,  *炭素 ,  加熱速度 ,  *放電プラズマ焼結 ,  感受性 ,  蒸発 ,  スピネル ,  急速加熱
準シソーラス用語： カーボン紙 ,  焼結温度 ,  *炭素汚染 ,  *酸化物セラミックス , 【Automatic Indexing@JST】

著者キーワード (4件)： 放電プラズマ焼結 ,  炭素 ,  光学的性質 ,  Spinels

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (5件)： スパークプラズマ焼結 ,  SPS ,  酸化物セラミックス ,  炭素汚染 ,  分布