Ti-6Al-4V合金のワイヤアーク添加物製造のミクロ組織と引張特性に及ぼす溶融池サイズの影響【JST・京大機械翻訳】

Effect of Molten Pool Size on Microstructure and Tensile Properties of Wire Arc Additive Manufacturing of Ti-6Al-4V Alloy

著者 (7件)： Wu Qianru (School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China) ,  Lu Jiping (School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China) ,  Liu Changmeng (School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China) ,  Fan Hongli (School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China) ,  Shi Xuezhi (School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China) ,  Fu Jie (School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China) ,  Ma Shuyuan (School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China)
資料名： Materials (Web)  (Materials (Web))
巻： 10  号： 7  ページ： 749  発行年： 2017年 
JST資料番号： U7237A  ISSN： 1996-1944  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： ワイヤアーク付加製造(WAAM)技術は,産業領域における大きな構造部品を製造するためのコスト競争力があり,効率的な技術である。機械的性質は主に成分の微細構造によって支配され,それは溶融池サイズによって深く影響される。本研究では,成分の微細構造と機械的性質に及ぼす溶融池サイズの影響を調べるために,7mmから22mmまでの範囲の異なる幅の溶融池(WMP)を有する一連のTi-6Al-4V合金ブロックを,ワイヤ供給速度(WFS)を100cm/分から500cm/分まで調整することによって蒸着した。マクロ構造は柱状結晶粒から等軸結晶粒に変化し,WMPの増加により大きな柱状結晶粒に戻り,それは主に異なる冷却速度と熱勾配により引き起こされることを見出すことは興味深い。それにもかかわらず,成分の引張特性はWMPの増加とともに減少する傾向を有した。Copyright 2018 The Author(s) All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 微細構造 ,  柱状晶 ,  温度勾配 ,  冷却速度 ,  *合金 ,  *Ti-6Al-4V合金 ,  付加製造 ,  マクロ組織 ,  結晶粒 ,  *溶融池 ,  機械的性質
準シソーラス用語： *引張特性 , 【Automatic Indexing@JST】

著者キーワード (5件)： ワイヤアーク添加物製造 ,  Ti-6Al-4V ,  溶融池サイズ ,  微細構造 ,  引張特性

分類 (3件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U) ,  溶接技術  (WC07030G)

引用文献 (24件)：

• Wang, H.; Jiang, W.; Ouyang, J.; Kovacevic, R. Rapid prototyping of 4043 Al-alloy parts by vp-gtaw. J. Mater. Process. Technol. 2004, 148, 93-102.
• Baufeld, B.; Biest, O.V.D.; Gault, R. Additive manufacturing of Ti-6AL-4V components by shaped metal deposition: Microstructure and mechanical properties. Mater. Des. 2010, 31, S106-S111.
• Ding, D.; Pan, Z.; Cuiuri, D.; Li, H. A tool-path generation strategy for wire and arc additive manufacturing. Int. J. Adv. Manuf. Technol. 2014, 73, 173-183.
• Shi, X.; Ma, S.; Liu, C.; Wu, Q.; Lu, J.; Liu, Y.; Shi, W. Selective laser melting-wire arc additive manufacturing hybrid fabrication of Ti-6AL-4V alloy: Microstructure and mechanical properties. Mater. Sci. Eng. 2017, 684, 196-204.
• Acharya, R.; Das, S. Additive manufacturing of in 100 superalloy through scanning laser epitaxy for turbine engine hot-section component repair: Process development, modeling, microstructural characterization, and process control. Metall. Mater. Trans. A 2015, 46, 3864-3875.

タイトルに関連する用語 (8件)： Ti-6Al-4V合金 ,  ワイヤ ,  アーク ,  添加物 ,  ミクロ組織 ,  引張特性 ,  溶融池 ,  サイズ