Pt/Co/Au/Cr_2O_3/Pt積層膜における磁気-電場冷却により逆転した反強磁性ドメインのフラストレーションと緩和【JST・京大機械翻訳】

Frustration and relaxation of antiferromagnetic domains reversed by magneto-electric field cooling in a Pt/Co/Au/Cr₂O₃/Pt-stacked film

著者 (5件)： Shiratsuchi Yu (Department of Materials Science and Engineering, Graduate School of Engineering, Osaka University, Suita, Osaka 565-0871, Japan) ,  Watanabe Shunsuke (Department of Materials Science and Engineering, Graduate School of Engineering, Osaka University, Suita, Osaka 565-0871, Japan) ,  Yonemura Shogo (Advanced Technology Development Center, TDK Corporation, Chiba 272-0026, Japan) ,  Shibata Tatsuo (Advanced Technology Development Center, TDK Corporation, Chiba 272-0026, Japan) ,  Nakatani Ryoichi (Department of Materials Science and Engineering, Graduate School of Engineering, Osaka University, Suita, Osaka 565-0871, Japan)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 8  号： 12  ページ： 125313-125313-9  発行年： 2018年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 磁気領域観測を用いて,磁気-電場冷却(MEFC)により駆動される反強磁性Cr_2O_3分域反転から生じる垂直交換バイアス極性の反転過程を調べた。交換バイアス極性はMEFC中の電場の増加とともに負から正に変化した。磁区の関連変化は正の交換バイアスを示す逆磁区の確率的出現を明らかにした。局所磁化曲線は,MEFC後の反強磁性ドメイン状態が,界面交換結合とバルク磁気電気効果の間のエネルギー競合のためにフラストレーションされたことを示唆した。磁気ドメイン構造のフラストレーション特性は,MEFC後の交換バイアスの訓練効果によって支持される。Copyright 2019 AIP Publishing LLC All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *欲求不満 ,  磁区 ,  *電場 ,  *反強磁性 ,  界面 ,  *磁気 ,  磁気電気効果 ,  反転過程 ,  極性 ,  分域 ,  *多層膜
準シソーラス用語： 交換結合 ,  磁化曲線 ,  交換バイアス ,  *ドメイン構造 , 【Automatic Indexing@JST】

分類 (4件)： 金属の磁区及び磁化過程  (BM06112D) ,  磁区・磁化過程一般  (BM06111M) ,  磁性材料  (NA04040H) ,  酸化物結晶の磁性  (BM06050E)

タイトルに関連する用語 (11件)： Pt ,  CO ,  Au ,  積層膜 ,  磁気 ,  電場 ,  逆転 ,  反強磁性 ,  ドメイン ,  フラストレーション ,  緩和