高性能Li-O_2電池用の絹繭から得た窒素ドープ多孔質炭素【JST・京大機械翻訳】

Nitrogen-doped Porous Carbon Obtained from Silk Cocoon for High Performance Li-O₂ Batteries

著者 (7件)： Liu Jiuqing (School of Metallurgy and Environment, Cental South University, Hunan, Changsha, 410083, China) ,  Zhao Haijun (School of Metallurgy and Environment, Cental South University, Hunan, Changsha, 410083, China) ,  Zhu Fangfang (School of Metallurgy and Environment, Cental South University, Hunan, Changsha, 410083, China) ,  Yu Wanjing (School of Metallurgy and Environment, Cental South University, Hunan, Changsha, 410083, China) ,  Li Jie (School of Metallurgy and Environment, Cental South University, Hunan, Changsha, 410083, China) ,  Li Qihou (School of Metallurgy and Environment, Cental South University, Hunan, Changsha, 410083, China) ,  Wang Cheng (School of Metallurgy and Environment, Cental South University, Hunan, Changsha, 410083, China)
資料名： Chemistryselect  (Chemistryselect)
巻： 4  号： 25  ページ： 7602-7608  発行年： 2019年 
JST資料番号： W2528A  ISSN： 2365-6549  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 絹繭(NCFC)から得られた窒素ドープ多孔質炭素を,本論文においてイオン液体を有するLi-O_2電池のためのカソードとして最初に用いた。NCFCは不規則な曲げスライスから作られ,電気化学反応のための多数の活性サイトを意味する2142.0m~2g~(-1)の大部分のLi-O2表面積の高い比放電生成物を有している。結果は,NCFCベースのLi-O_2電池には,種々の電流密度の下で良いサイクル安定性と高いエネルギー効率があることを示している。特に,NCFCベースのLi-O_2電池は,最大過電圧が0.92V未満の400サイクル(500mAhg(-1))以上で,超PベースのLi-O_2電池よりもはるかに優れている(1.88Vまでの過電圧で188サイクル),多くの報告されているLi-O_2電池である。結果は,NCFCがLi-O_2電池のための非常に有望な材料であることを示した。Copyright 2019 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 放電 ,  *絹 ,  電気化学反応 ,  *電池 ,  電流密度 ,  過電圧 ,  表面積 ,  カソード ,  活性部位 ,  エネルギー効率 ,  イオン液体
準シソーラス用語： サイクル安定性 ,  *多孔質炭素 ,  *窒素ドーピング , 【Automatic Indexing@JST】

著者キーワード (5件)： Li-O2電池 ,  絹繭 ,  窒素ドープ多孔質炭素 ,  炭素材料 ,  サイクル性能