工業-海洋大気環境におけるPH13-8Moステンレス鋼の腐食挙動に及ぼす予備不動態化の影響【JST・京大機械翻訳】

Effect of Pre-passivation on the Corrosion Behavior of PH13-8Mo Stainless Steel in Industrial-Marine Atmospheric Environment

著者 (6件)： Liu Yanning (Corrosion and Protection Center, University of Science and Technology Beijing, Beijing, China) ,  Zhao Qiyue (Corrosion and Protection Center, University of Science and Technology Beijing, Beijing, China) ,  Zhao Jinbin (Jiangsu Key Laboratory for Premium Steel Material, Technology Center of Nanjing Iron & Steel Co., Ltd., Nanjing, China) ,  Huang Yunhua (Corrosion and Protection Center, University of Science and Technology Beijing, Beijing, China) ,  Cheng Xuequn (Corrosion and Protection Center, University of Science and Technology Beijing, Beijing, China) ,  Lu Lin (Corrosion and Protection Center, University of Science and Technology Beijing, Beijing, China)
資料名： Frontiers in Materials (Web)  (Frontiers in Materials (Web))
巻： 6  ページ： 296  発行年： 2019年 
JST資料番号： U7077A  ISSN： 2296-8016  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 形態学的観察,重量損失測定,X線光電子分光法(XPS)および走査Kelvinプローブ(SKP)を用いて,青島の工業-海洋大気環境における5年間の屋外曝露試験を通して,硝酸不動態化膜の有無によるPH13-8Moステンレス鋼の腐食挙動および機構を研究した。結果は,予備不動態化が腐食を確実に抑制するが,工業-海洋大気中のPH13-8Moステンレス鋼の保護期間の明らかな限界を示すことを示した。裸のPH13-8Mo鋼と比較して,予備不動態化鋼の孔食の数と深さは減少し,平均腐食速度は14.7%減少した。改善された耐食性の理由は,Cr/Feと酸化物/水酸化物の高い比率,および屋外曝露された予備不動態化鋼の表面に対するより正で均一なKelvin電圧電位を含んでいた。一方,Crに富む析出相によって引き起こされたCr枯渇領域上の予備不動態化膜は,Cl-によって大気中で優先的に破壊され,それは保護期間を減少させた。Copyright 2019 The Author(s) All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 鉄 ,  クロム ,  *鋼 ,  水酸化物 ,  腐食速度 ,  硝酸 ,  走査 ,  *ステンレス鋼 ,  X線光電子分光法 ,  電圧 ,  酸化物 ,  *海洋大気 ,  不動態皮膜 ,  *不動態化 ,  耐食性

著者キーワード (5件)： PH13-8Moステンレス鋼 ,  予備不動態化処理 ,  大気腐食 ,  孔食 ,  表面電位

分類 (5件)： 用途開発  (YM01080Z) ,  下水,廃水の化学的処理  (SC03050W) ,  その他の特殊構造物  (RA05020W) ,  廃水処理  (YM01030W) ,  音波伝搬  (BB03030G)

引用文献 (44件)：

• Bonagani S. K., Bathula V., Kain V. (2018). Influence of tempering treatment on microstructure and pitting corrosion of 13 wt.% Cr martensitic stainless steel. Corros. Sci. 131, 340-354. doi: 10.1016/j.corsci.2017.12.012
• Button H. E., Simm D. W. (1985). The influence of particulate matter on the corrosion behaviour of type 316 stainless steel. Anti Corros. Methods Mater. 32, 8-10. doi: 10.1108/eb020346
• Carmezim M. J., Simões A. M., Montemor M. F., Belo M. D. C. (2005). Capacitance behaviour of passive films on ferritic and austenitic stainless steel. Corros. Sci. 47, 581-591. doi: 10.1016/j.corsci.2004.07.002
• Chen X., Li X. G., Du C. W., Z Cheng Y. F. (2009). Effect of cathodic protection on corrosion of pipeline steel under disbonded coating. Corros. Sci. 51, 2242-2245. doi: 10.1016/j.corsci.2009.05.027
• Cheng X. Q., Li X. G., Dong C. F. (2009). Study on the passive film formed on 2205 stainless steel in acetic acid by AAS and XPS. Inter. J. Miner. Metall. Mater. 16, 170-176. doi: 10.1016/S1674-4799(09)60029-7

タイトルに関連する用語 (6件)： 工業 ,  海洋 ,  大気環境 ,  ステンレス鋼 ,  腐食挙動 ,  不動態化