無電解金属めっきのためのABS樹脂表面の光酸化【JST・京大機械翻訳】

Photooxidation of the ABS resin surface for electroless metal plating

著者 (6件)： Jia Yankun (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, Yamadaoka 2-1, Suita, Osaka, 565-0871, Japan) ,  Chen Jiaxin (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, Yamadaoka 2-1, Suita, Osaka, 565-0871, Japan) ,  Asahara Haruyasu (Graduate School of Pharmaceutical Sciences, Osaka University, Yamadaoka 1-6, Suita, Osaka, 565-0871, Japan) ,  Hsu Yu-I (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, Yamadaoka 2-1, Suita, Osaka, 565-0871, Japan) ,  Asoh Taka-Aki (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, Yamadaoka 2-1, Suita, Osaka, 565-0871, Japan) ,  Uyama Hiroshi (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, Yamadaoka 2-1, Suita, Osaka, 565-0871, Japan)
資料名： Polymer  (Polymer)
巻： 200  ページ： Null  発行年： 2020年 
JST資料番号： D0472B  ISSN： 0032-3861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,ABS樹脂の表面を酸化するために,光活性化二酸化塩素ラジカル(ClO_2・)を用いたクリーンで,効果的で低コストの改質法を適用した。酸素含有基のポリブタジエン(PB)への取り込みとABS樹脂の表面親水性の改善から生じる表面極性基の量の増加を酸化後に観察した。酸化ABS樹脂は無電解金属めっき後に金属層に良好な接着性を示した。この方法は無電解めっきのための効果的なアプローチとして応用できた。表面改質と無電解めっきに及ぼす酸化時間と温度の影響の研究は,室温での10分間の酸化の穏やかな条件が最適であることを示した。さらに,光照射がこのプロセスによるプラスチックの改質に必要でなかったので,この改質法は複雑な形状を有するABS樹脂に成功裏に使用され,その実用的適用性を広げた。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *酸化 ,  *電解 ,  プラスチック ,  酸素 ,  *ABS樹脂 ,  無電解めっき ,  *光酸化 ,  光照射 ,  親水性 ,  二酸化塩素 ,  表面改質
準シソーラス用語： 粘着性 ,  光活性化 ,  極性基 ,  金属めっき , 【Automatic Indexing@JST】

著者キーワード (3件)： ABS樹脂 ,  光酸化 ,  無電解金属めっき

分類 (4件)： 高分子固体の構造と形態学  (CG02022M) ,  高分子固体の物理的性質  (CG02024U) ,  高分子固体の力学的性質  (CG02023D) ,  エポキシ樹脂  (YH07040I)

タイトルに関連する用語 (4件)： 電解 ,  金属めっき ,  ABS樹脂 ,  光酸化