Cu-O鎖中の酸素を含まないLu_0.5Ca_0.5Ba_1.4Sr_0.6Cu_3O_6のRE-123相における超伝導【JST・京大機械翻訳】

Superconductivity in the RE-123 phase of Lu_0.5Ca_0.5Ba_1.4Sr_0.6Cu₃O₆ without oxygen in the Cu-O chain

著者 (4件)： Nakagawa Kohei (Department of Applied Physics, Graduate School of Engineering, Tohoku University, 6-6-05 Aoba, Aramaki, Aoba-ku, Sendai 980-8579, Japan) ,  Noji Takashi (Department of Applied Physics, Graduate School of Engineering, Tohoku University, 6-6-05 Aoba, Aramaki, Aoba-ku, Sendai 980-8579, Japan) ,  Kawamata Takayuki (Department of Applied Physics, Graduate School of Engineering, Tohoku University, 6-6-05 Aoba, Aramaki, Aoba-ku, Sendai 980-8579, Japan) ,  Kato Masatsune (Department of Applied Physics, Graduate School of Engineering, Tohoku University, 6-6-05 Aoba, Aramaki, Aoba-ku, Sendai 980-8579, Japan)
資料名： Physica C. Superconductivity and Its Applications  (Physica C. Superconductivity and Its Applications)
巻： 568  ページ： Null  発行年： 2020年 
JST資料番号： T0580A  ISSN： 0921-4534  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 通常の固相反応法により,いわゆるCu(1)O鎖のブロッキング層中に酸素を含まないLu_0.5Ca_0.5Ba_1.4Sr_0.6Cu_3O_6の多結晶試料を調製した。5.87の酸素含有量を有する試料の磁化率測定で観察された超伝導転移T_c~開始=80Kの開始温度は,REBA_2Cu_3O_6(RE:希土類元素)相で最も高い記録であった。R.T.での熱起電力から推定した超伝導Cu(2)O_2面の正孔濃度は約0.12(/Cu(2))であり,試料がまだアンダードープ領域に位置していることを示した。T_cに及ぼすブロッキング層への酸素導入の影響も調べた。T_cは,Lu_0.5Ca_0.5Ba_1.4Sr_0.6Cu_3O_6+_δにおいて,6+δ6.1で最小値を,6+δ6.5で最大値をとることがわかった。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *酸素 ,  多結晶 ,  固相反応 ,  磁化率 ,  熱起電力 ,  *超伝導
準シソーラス用語： 超伝導転移温度 ,  酸化物超伝導体 ,  正孔濃度 ,  超伝導転移 ,  酸素含有量 ,  ブロッキング層 , 【Automatic Indexing@JST】

著者キーワード (5件)： 酸化物超伝導体 ,  RE-123構造 ,  元素置換 ,  超伝導転移温度 ,  ホール濃度

分類 (1件)： 酸化物系超伝導体の物性  (BM04023I)

タイトルに関連する用語 (3件)： Cu ,  酸素 ,  伝導