電気めっき法により作製したFe-Pt膜磁石の高温特性【JST・京大機械翻訳】

High-temperature properties of Fe-Pt film-magnets prepared by electroplating method

著者 (8件)： Yanai Takeshi (Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Omagari Yuya (Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Furutani Seiya (Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Yamashita Akihiro (Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Fujita Naoyuki (National Institute of Technology, Nara College, 22 Yata-cho, Yamatokori, Yamatokoriyama, Nara 639-1080, Japan) ,  Morimura Takao (Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Nakano Masaki (Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan) ,  Fukunaga Hirotoshi (Nagasaki University, 1-14 Bunkyo-machi, Nagasaki 852-8521, Japan)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 10  号： 1  ページ： 015149-015149-5  発行年： 2020年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 電気めっき法を用いてCu基板上にL1_0規則化Fe_50pT_50厚膜を調製し,25~200°Cの温度範囲でそれらの高温特性を評価した。通常のアニーリング法(700°C,60分)でアニールしたFe_50pT_50膜に対する150°CでのHcと(BH)_maxは,それぞれ500kA/mと50kJ/m3で,Hcの熱係数は-0.3%/°Cであった。高温特性を改善するために,赤外炉(8kW)を用いたフラッシュアニーリング法を用いた。フラッシュアニーリング法は高温特性(Hc=700kA/m,(BH)_max=70kJ/m3,150°C)と熱係数(-0.21%/°C)を改善した。膜の熱安定性はSm-Co系磁石の熱安定性に匹敵し,Nd-Fe-B系よりも優れていた。したがって,著者らは,電気めっきによって調製されたL1_0規則化Fe_50pT_50膜を発見し,フラッシュアニーリングは,広い温度範囲における有望な小型磁石の1つである。Copyright 2020 AIP Publishing LLC All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 赤外線 ,  シミュレーテッドアニーリング ,  厚膜 ,  *電気めっき ,  銅 ,  熱安定性 ,  *磁石 ,  焼なまし
準シソーラス用語： 温度範囲 ,  *高温特性 , 【Automatic Indexing@JST】

分類 (2件)： 酸化物結晶の磁性  (BM06050E) ,  金属結晶の磁性  (BM06040T)

タイトルに関連する用語 (6件)： 電気めっき法 ,  作製 ,  Fe ,  Pt ,  磁石 ,  高温特性