種々の条件下で過熱水蒸気処理を受けた再生炭素繊維の引張特性【JST・京大機械翻訳】

Tensile properties of recycled carbon fibers subjected to superheated steam treatment under various conditions

著者 (5件)： Cai Guangbin (Department of Systems Innovation, School of Engineering, The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-8656, Japan) ,  Wada Masashi (Japan Fine Ceramics Center, 2-4-1 Mutsuno, Atsuta-ku, Nagoya 456-8587, Japan) ,  Ohsawa Isamu (Department of Systems Innovation, School of Engineering, The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-8656, Japan) ,  Kitaoka Satoshi (Japan Fine Ceramics Center, 2-4-1 Mutsuno, Atsuta-ku, Nagoya 456-8587, Japan) ,  Takahashi Jun (Department of Systems Innovation, School of Engineering, The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-8656, Japan)
資料名： Composites. Part A. Applied Science and Manufacturing  (Composites. Part A. Applied Science and Manufacturing)
巻： 133  ページ： Null  発行年： 2020年 
JST資料番号： E0231D  ISSN： 1359-835X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 超加熱水蒸気(SHS)を含む新しい処理条件を提案し,繊維強度の最小の減少を伴う最適炭素繊維回収を達成した。一方向炭素繊維強化シートを,プロセスガスとしてN_2またはCO_2の添加により,650°Cで1時間SHSに暴露した。回収率を質量変化と熱重量分析及び示差走査熱量測定を用いて評価した。結果は,N_2の添加が繊維強度の減少を効率的に抑制し,最適回収を達成したことを示した。Weibullパラメータは,低強度繊維が狭い強度分布を示す傾向があることを示した。破面と斜め断面の観察は,酸化条件下での表面結晶の固有欠陥と腐食の存在が強度分布の劣化と変化の原因であることを示した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 機械的性質 ,  酸化 ,  *過熱蒸気 ,  熱重量分析 ,  *炭素繊維 ,  破面 ,  示差走査熱量測定 ,  回収率
準シソーラス用語： プロセスガス ,  強度分布 ,  *引張特性 ,  繊維強度 , 【Automatic Indexing@JST】

著者キーワード (4件)： A.炭素繊維 ,  B 機械的性質 ,  C 統計的性質/方法 ,  E.リサイクル

分類 (2件)： 機械的性質  (YH02022L) ,  繊維物理  (YM02020S)

タイトルに関連する用語 (3件)： 過熱水蒸気 ,  炭素繊維 ,  引張特性