Na_2O-B_2O_3-SiO_2ガラスフラックスを含むアルミナ血小板のカード集合体の成長機構【JST・京大機械翻訳】

Growth mechanism of house-of-cards aggregates of alumina platelets containing Na₂O-B₂O₃-SiO₂ glass flux

著者 (5件)： Muto Daimu (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, 466-8555, Japan) ,  Hashimoto Shinobu (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, 466-8555, Japan) ,  Daiko Yusuke (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, 466-8555, Japan) ,  Honda Sawao (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, 466-8555, Japan) ,  Iwamoto Yuji (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, 466-8555, Japan)
資料名： Ceramics International  (Ceramics International)
巻： 46  号： 7  ページ： 9109-9118  発行年： 2020年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 耐熱性耐火材料としての使用を意図した多孔質アルミナ体を高温蒸発法により作製し,特性化した。一連のフラックスシステムを,ホウ酸と炭酸ナトリウムに加えてNa_2O-B_2O_3ガラスに第三成分を添加することによって用いた。SiO_2を第3の成分として添加したとき,一次アルミナ粒子は異方性的に成長し,板状形状を形成し,カード構造を自己組織化した。アルミナ小板の異方性成長は,α-Al_2O_3表面上のフラックス中のSi4+イオンの固溶体によって促進された。さらに,アルミナ小板間の結合は,高SiO_2濃度フラックスによって強化された。著者らの典型的なアルミナ体は,1700°Cで再加熱したとき,71.5%の気孔率,3.7MPaの圧縮強度,2.6%の収縮率,および1000°Cで0.24Wm~1K~1の熱伝導率を有した。したがって,現在のアルミナ体は,高性能断熱耐火材料としての応用を見出すことが期待される。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 異方性 ,  *ガラス ,  高温 ,  固溶体 ,  蒸発 ,  熱伝導率 ,  *アルミナ ,  ホウ酸 ,  炭酸ナトリウム ,  *血小板 ,  圧縮強さ ,  自己組織化 ,  再加熱 ,  *凝集体
準シソーラス用語： 多孔質アルミナ , 【Automatic Indexing@JST】

著者キーワード (5件)： 多孔質アルミナ ,  形態学 ,  形成機構 ,  異方性成長 ,  断熱

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  耐火物  (YC04030N)

タイトルに関連する用語 (7件)： ガラス ,  フラックス ,  アルミナ ,  血小板 ,  カード ,  集合体 ,  成長