ゼラチンゾルを用いるプレートレットからなる高度に等方的な多孔質アルミナ耐火物クリンカの製造

Fabrication of highly isotropic porous alumina refractory clinkers consisting of platelets using a gelatin-sol

著者 (6件)： Muto Daimu (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Nagoya, Japan) ,  Hashimoto Shinobu (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Nagoya, Japan) ,  Kondo Hiroki (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Nagoya, Japan) ,  Daiko Yusuke (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Nagoya, Japan) ,  Honda Sawao (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Nagoya, Japan) ,  Iwamoto Yuji (Department of Life Science and Applied Chemistry, Nagoya Institute of Technology, Nagoya, Japan)
資料名： Journal of Asian Ceramic Societies (Web)  (Journal of Asian Ceramic Societies (Web))
巻： 8  号： 2  ページ： 265-276  発行年： 2020年 
JST資料番号： U1450A  ISSN： 2187-0764  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 多孔質アルミナ体は無機製品の製造の際のエネルギー消費を低減させる耐火物としての利用を見いだせると期待されている。このような物体の気孔率は,“house-of-cards”と呼ばれる構造を形成するアルミナプレートレットを用いることで効率的に増加させることができる。本研究において,ゼラチンゾル(結合剤として)と冷凍乾燥と共にこの技術を採用した。この方法で作製し,1600°Cで熱処理した多孔質アルミナの気孔率,圧縮強さ,および熱伝導率は,それぞれ,80.2%,1.7MPa,および0.94W/m^-1・K^-1であった。これらの物理化学的性質は,このアルミナを断熱耐火クリンカ材料として用いることを可能にさせるであろう。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.

シソーラス用語： *酸化アルミニウム ,  多孔質体 ,  クリンカ ,  結晶 ,  ゼラチン ,  粘結剤 ,  *凍結乾燥 ,  圧縮強さ ,  空隙率 ,  *熱伝導率 ,  *焼成 ,  板状結晶 ,  機械的性質 ,  強度

著者キーワード (5件)： 多孔性アルミナ ,  ハウスオブカード構造 ,  ゼラチン-ゾル ,  圧縮強度 ,  熱伝導率

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (5件)： ゼラチン ,  ゾル ,  多孔質アルミナ ,  耐火物 ,  クリンカ