セルロースナノファイバ強化澱粉フィルムの湿潤強度と耐久性に及ぼす澱粉老化の影響【JST・京大機械翻訳】

Effect of starch retrogradation on wet strength and durability of cellulose nanofiber reinforced starch film

著者 (5件)： Soni Raghav (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka, 565-0871, Japan) ,  Asoh Taka-Aki (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka, 565-0871, Japan) ,  Hsu Yu-I (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka, 565-0871, Japan) ,  Shimamura Michiyo (Planning Department, Japan Agency for Marine-Earth Science and Technology (JAMSTEC), Natsushima-cho 2-15, Yokosuka, Tokyo, 237-0061, Japan) ,  Uyama Hiroshi (Department of Applied Chemistry, Graduate School of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka, 565-0871, Japan)
資料名： Polymer Degradation and Stability  (Polymer Degradation and Stability)
巻： 177  ページ： Null  発行年： 2020年 
JST資料番号： E0404B  ISSN： 0141-3910  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 適切な機械的性質と耐水性を有するセルロースナノ繊維強化老化澱粉フィルムを調製した。非老化タピオカ澱粉(NRS)と老化したタピオカ澱粉(RS)を,異なる重量比でTEMPO酸化セルロースナノ繊維(TCNF)と混合した。続いて,懸濁液を溶液キャスティング法を用いて膜にキャストした。TCNF/RS膜は,TCNF/NRS膜と比較して,水中での膨潤の減少と機械的強度の向上を示した。X線回折により,老化澱粉の導入による結晶化度の改善が確認され,接触角試験は,老化澱粉混合フィルムが高い耐水性を有することを示した。これらの結果は,老化澱粉混合TCNFフィルム(TCNF/RS)が単一使用石油化学プラスチック包装フィルムを代替する可能性を有することを示唆した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  機械的性質 ,  懸濁液 ,  接触角 ,  膨潤 ,  *澱粉 ,  石油化学 ,  結晶度 ,  タピオカ ,  *湿潤強さ ,  *澱粉老化 ,  機械的強度
準シソーラス用語： 質量比 ,  TEMPO酸化 ,  *セルロースナノファイバー , 【Automatic Indexing@JST】

著者キーワード (4件)： 老化澱粉 ,  セルロースナノ繊維 ,  包装フィルム ,  湿潤強度

分類 (2件)： 高分子の分解,劣化  (CG03010A) ,  抵抗性  (YH02050K)

タイトルに関連する用語 (6件)： セルロースナノファイバ ,  強化 ,  澱粉 ,  フィルム ,  湿潤強度 ,  澱粉老化