Corrosion performance of DLC coatings with laser-induced graphitized periodic surface structure

著者 (7件)： Yasumaru Naoki (National Institute of Technology, Fukui College, Sabae, Fukui 916-8507, Japan) ,  Kasashima Haruka (Kawasaki Heavy Industries, Ltd., Gifu Works, Kagamihara, Gifu 504-8710, Japan) ,  Sentoku Eisuke (National Institute of Technology, Fukui College, Sabae, Fukui 916-8507, Japan) ,  Funabora Hisato (National Institute of Technology, Fukui College, Sabae, Fukui 916-8507, Japan) ,  Tominaga Ryoya (Toyohashi University of Technology, Toyohashi, Aichi 441-8580, Japan) ,  Harigai Toru (Toyohashi University of Technology, Toyohashi, Aichi 441-8580, Japan) ,  Takikawa Hirofumi (Toyohashi University of Technology, Toyohashi, Aichi 441-8580, Japan)
資料名： Diamond and Related Materials  (Diamond and Related Materials)
巻： 109  ページ： Null  発行年： 2020年 
JST資料番号： W0498A  ISSN： 0925-9635  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 2種類のダイヤモンド状炭素(DLC)薄膜,水素化非晶質炭素(a-C:H)および超硬質四面体非晶質炭素(ta-C)をフェムト秒レーザパルスで照射し,レーザ誘起周期的表面構造(LIPSS)およびナノ結晶グラファイト(nc-G)に修飾したDLC膜の耐食性をアノード分極測定から電気化学的に評価した。nc-Gの型であるガラス状炭素(GC)板の分極曲線を比較のために測定した。LIPSSを有するステンレス鋼の分極曲線も測定し,LIPSSが照射部分の表面積を増加させ,見かけの腐食電流密度の増加をもたらすことを確認した。照射DLCの分極曲線測定は,LIPSSの形成による表面積の増加の影響にもかかわらず,腐食電流密度が減少し,分極曲線がGCプレートのそれらに近づく傾向があることを示した。したがって,DLCの照射表面層はnc-Gに改質され,GCと類似の優れた耐食性をもたらす。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *表面構造 ,  *腐食 ,  ステンレス鋼 ,  耐食性 ,  水素化 ,  グラファイト ,  陽分極 ,  電気化学 ,  腐食電流 ,  DLC膜 ,  ナノ結晶 ,  フェムト秒レーザ
準シソーラス用語： *レーザ誘起 ,  分極曲線 ,  アモルファスカーボン , 【Automatic Indexing@JST】

著者キーワード (5件)： フェムト秒レーザ加工 ,  レーザ誘起周期的表面構造 ,  黒鉛化 ,  DLC ,  腐食

分類 (2件)： 炭素とその化合物  (YB02060D) ,  金属材料へのセラミック被覆  (YC02050V)

タイトルに関連する用語 (5件)： レーザ誘起 ,  黒鉛化 ,  表面構造 ,  DLC被覆 ,  腐食