WO_3-La_2O_3-B_2O_3-Nb_2O_5ガラスの構造研究【JST・京大機械翻訳】

Structural study of WO₃-La₂O₃-B₂O₃-Nb₂O₅ glasses

著者 (5件)： Iordanova Reni (Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, G. Bonchev, str. bld. 11, 1113 Sofia, Bulgaria) ,  Milanova Margarita (Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, G. Bonchev, str. bld. 11, 1113 Sofia, Bulgaria) ,  Aleksandrov Lyubomir (Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, G. Bonchev, str. bld. 11, 1113 Sofia, Bulgaria) ,  Shinozaki Kenji (National Institute of Advanced Industrial Science and Technology (AIST), 1-8-31 Midorigaoka, Ikeda, Osaka 563-8577, Japan) ,  Komatsu Takayuki (Department of Materials Science and Technology, Nagaoka University of Technology, 1603-1 Kamitomioka-cho, Nagaoka 940-2188, Japan)
資料名： Journal of Non-Crystalline Solids  (Journal of Non-Crystalline Solids)
巻： 543  ページ： Null  発行年： 2020年 
JST資料番号： D0642A  ISSN： 0022-3093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： WO_3-La_2O_3-B_2O_3ガラスへのNb_2O_5の添加が,それらの構造および物理的性質(密度,モル体積,ガラス転移温度)に及ぼす影響を,IRおよびRaman分光法,密度測定およびDTA分析を用いて調べた。RamanとIRスペクトルは,ニオブイオンが,コーナーとエッジによって相互接続されたNbO_6八面体として,塩基タングステン酸塩ガラスマトリックスに取り込まれることを明らかにした。低いNb_2O_5含有量(10mol%)では,ガラスネットワーク中に多数の混合B-O-NbとW-O-Nb結合が存在した。Nb_2O_5濃度(15mol%と20mol%)の増加と共に,これらの結合は,コーナー共有NbO_6八面体間のNb-O-Nb結合によって徐々に置換され,3Dクラスタを形成し,主にLa-O-Nb結合の非晶質ネットワークに組み込まれた。10mol%以上の酸化ニオブの添加はガラスの熱安定性を低下させ,酸化ニオブ多面体クラスタの形成に関連する密度を増加させた。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： Ramanスペクトル ,  イオン ,  *ガラス ,  示差熱分析 ,  赤外スペクトル ,  ネットワーク ,  *ニオブ ,  相互接続 ,  ガラス転移点 ,  酸化ニオブ ,  タングステン酸塩 ,  非晶質 ,  クラスタ ,  三次元 ,  Raman分光法

著者キーワード (4件)： ガラス ,  構造 ,  Ramanスペクトル ,  IRスペクトル

分類 (1件)： ガラスの性質・分析・試験  (YC02030Z)

タイトルに関連する用語 (2件)： ガラス ,  研究