リチウムイオン電池の熱暴走特性に及ぼす凍結処理の影響【JST・京大機械翻訳】

Influence of Freezing Treatment on the Thermal Runaway Characteristics of Lithium-Ion Batteries

著者 (7件)： Wweng J (State Key Laboratory of Fire Science, University of Science and Technology of China, Hefei, 230026, China) ,  Wweng J (Department of Civil and Architectural Engineering, City University of Hong Kong, Hong Kong, 999077, China) ,  Ouyang D X (State Key Laboratory of Fire Science, University of Science and Technology of China, Hefei, 230026, China) ,  Chen MY (School of Environment and Safety Engineering, University of Jiangsu, Zhenjiang, 212013, China) ,  Ding C (State Key Laboratory of Fire Science, University of Science and Technology of China, Hefei, 230026, China) ,  Ding C (School of Environment and Energy Engineering, Anhui Jianzhu University, Hefei 230601, China) ,  Wang J (State Key Laboratory of Fire Science, University of Science and Technology of China, Hefei, 230026, China)
資料名： IOP Conference Series: Earth and Environmental Science  (IOP Conference Series: Earth and Environmental Science)
巻： 581  号： 1  ページ： 012013 (8pp)  発行年： 2020年 
JST資料番号： W5558A  ISSN： 1755-1307  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： リチウムイオン電池(LIB)の応用増加により,LIB輸送や貯蔵の実現可能な方法として提案されているフラッシュ凍結のような極端な条件下でのLIBの熱暴走(TR)挙動を調べる価値がある。本研究では,凍結処理の有無での電池のTR挙動を調べ,比較するために一連の実験を行った。その結果,凍結処理後の電池はより速い温度上昇を示し,TR(t)の開始時間は短縮した。例えば,tはブランク試験で277.2sであったが,72h凍結後の電池ではtは250.2sであった。さらに,TR後の内部電極材料の微細構造比較は,凍結処理がそれらの凝集とクラスタ化を悪化させることを示した。さらに,著者らは,凍結または極端な低温条件でも,より低い充電状態(SOC)でLIBを貯蔵する。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 低温 ,  *電池 ,  微細構造 ,  *凍結 ,  クラスタ化 ,  ブランク ,  フラッシュ蒸発 ,  昇温 ,  *リチウムイオン電池 ,  *熱暴走 ,  充電率 ,  改変
準シソーラス用語： 充電状態 ,  内部電極 , 【Automatic Indexing@JST】

分類 (1件)： 二次電池  (YB04030K)

タイトルに関連する用語 (3件)： リチウムイオン電池 ,  熱暴走 ,  凍結