擬容量ナノ粒子/秩序化配位子中間層における選択的CO_2電極触媒【JST・京大機械翻訳】

Selective CO₂ electrocatalysis at the pseudocapacitive nanoparticle/ordered-ligand interlayer

著者 (23件)： Kim Dohyung (Department of Materials Science and Engineering, University of California, Berkeley, CA, USA) ,  Kim Dohyung (Department of Chemistry, University of California, Berkeley, CA, USA) ,  Kim Dohyung (Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Yu Sunmoon (Department of Materials Science and Engineering, University of California, Berkeley, CA, USA) ,  Yu Sunmoon (Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Zheng Fan (Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Zheng Fan (Joint Center for Artificial Photosynthesis, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Roh Inwhan (Department of Chemistry, University of California, Berkeley, CA, USA) ,  Roh Inwhan (Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Li Yifan (Department of Chemistry, University of California, Berkeley, CA, USA) ,  Li Yifan (Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Louisia Sheena (Department of Chemistry, University of California, Berkeley, CA, USA) ,  Louisia Sheena (Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Qi Zhiyuan (Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Somorjai Gabor A. (Department of Chemistry, University of California, Berkeley, CA, USA) ,  Somorjai Gabor A. (Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Frei Heinz (Molecular Biophysics and Integrated Bioimaging Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Wang Lin-Wang (Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Wang Lin-Wang (Joint Center for Artificial Photosynthesis, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Yang Peidong (Department of Materials Science and Engineering, University of California, Berkeley, CA, USA) ,  Yang Peidong (Department of Chemistry, University of California, Berkeley, CA, USA) ,  Yang Peidong (Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA, USA) ,  Yang Peidong (Kavli Energy NanoScience Institute, Berkeley, CA, USA)
資料名： Nature Energy  (Nature Energy)
巻： 5  号： 12  ページ： 1032-1042  発行年： 2020年 
JST資料番号： W4777A  ISSN： 2058-7546  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 酵素は活性部位周辺の多重成分の協奏的操作を特徴とし,精巧な触媒特異性をもたらす。合成触媒表面上のそのような配置の実現は,理解がなされていない。ここでは,高特異性CO_2電極触媒のための多成分触媒ポケットを含むナノ粒子/秩序化配位子中間層を報告する。ナノ粒子/秩序化配位子中間層は,金属ナノ粒子表面と,その近傍での配位子の脱離層から成る。この中間層は,脱溶媒和カチオンが層間挿入された特異な擬似容量特性を有し,触媒ターンオーバーを,それぞれ,2桁および1桁の大きさで,元の金属表面および結合配位子を有するナノ粒子に対して1桁増強する,活性部位構造を生成した。ナノ粒子/秩序化配位子中間層を,水性条件で,限界過電圧で99%までのCO選択性と27mVの低い開始過電圧で,いくつかの金属にわたって実証した。さらに,中性媒質によるガス拡散環境において,ナノ粒子/秩序化配位子中間層は,高い電流密度(400mAcm-2で98.1%)で,ほぼ単位CO選択性を達成した。酵素中に見出された複合体,多成分環境は,高い触媒特異性を誘導するが,合成触媒では達成が困難である。現在,研究者は,CO_2電解還元を促進するポケットを生成するナノ粒子表面より上の配位子の動的,秩序化層から成る触媒を報告する。Copyright The Author(s), under exclusive licence to Springer Nature Limited 2020 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 脱着 ,  過電圧 ,  酵素 ,  カソード還元 ,  活性部位 ,  媒質 ,  多重化 ,  *電極触媒 ,  複合体 ,  カチオン ,  ターンオーバー ,  インターカレーション ,  *ナノ粒子
準シソーラス用語： 金属ナノ粒子 ,  擬似容量 , 【Automatic Indexing@JST】

分類 (1件)： 貴金属触媒  (CB06122I)

タイトルに関連する用語 (5件)： ナノ粒子 ,  秩序化 ,  配位子 ,  中間層 ,  電極触媒