多結晶炭化ほう素バルクにおける超高温曲げと歪駆動非晶質化【JST・京大機械翻訳】

Ultra-high temperature flexure and strain driven amorphization in polycrystalline boron carbide bulks

著者 (7件)： Demirskyi D. (Advanced Institute for Materials Research (AIMR), Tohoku University, 2-1-1 Katahira, Aoba-ku, Sendai 980-8577, Japan) ,  Demirskyi D. (Department of Materials Science and Engineering, Tohoku University, 6-6-02 Aramaki Aza Aoba, Sendai 980-8579, Japan) ,  Demirskyi D. (National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan) ,  Sepehri-Amin H. (National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan) ,  Suzuki T.S. (National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan) ,  Yoshimi K. (Department of Materials Science and Engineering, Tohoku University, 6-6-02 Aramaki Aza Aoba, Sendai 980-8579, Japan) ,  Vasylkiv O. (National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 210  ページ： Null  発行年： 2022年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 焼結炭化ホウ素の曲げ強さの温度依存性を研究した。2000°C以上の温度では,B_4Cは1GPaを超える超曲げ強度を示し,脆性破壊から塑性変形への変形機構の変化を伴った。走査型透過電子顕微鏡(STEM)観察は,非晶質化が,2000°C以上の温度でのB_4Cの観察された塑性と310-3s-1の歪速度のミクロ組織の起源であることを明らかにした。非晶質化は,激しく変形した結晶粒の内部で起こる。2000°C以下の曲げ試験は,曲げ試験後の通常の欠陥である積層欠陥あるいは転位の形成の証拠を与えた。2000°Cでの結果は,変形過程で変形中にB_4C粒に課された引張応力の大きさが,変形過程でセラミックに転移した全歪が,結晶-非晶質変態において支配的な役割を果たすことを示唆する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 塑性 ,  焼結 ,  セラミック ,  変形 ,  曲げ試験 ,  温度依存性 ,  *超高温 ,  *非晶質 ,  *多結晶 ,  結晶粒 ,  曲げ強さ ,  塑性変形 ,  引張応力 ,  *炭化ホウ素 ,  *アモルファス化

著者キーワード (4件)： 炭化ホウ素 ,  透過電子顕微鏡(TEM) ,  結晶欠陥 ,  高温変形