還元拡散プロセスにより調製したSmリッチ層を有する高保磁力SmFe_10V_2粉末【JST・京大機械翻訳】

High-coercivity SmFe₁₀V₂ powder with Sm-rich layers prepared by a reduction-diffusion process

著者 (4件)： Zhao Luo (Department of Materials Science, Graduate School of Engineering, Tohoku University, 6-6-02 Aoba-yama, Sendai, Miyagi 980-8579, Japan) ,  Matsuura Masashi (Department of Materials Science, Graduate School of Engineering, Tohoku University, 6-6-02 Aoba-yama, Sendai, Miyagi 980-8579, Japan) ,  Yamamoto Kuniko (Department of Materials Science, Graduate School of Engineering, Tohoku University, 6-6-02 Aoba-yama, Sendai, Miyagi 980-8579, Japan) ,  Sugimoto Satoshi (Department of Materials Science, Graduate School of Engineering, Tohoku University, 6-6-02 Aoba-yama, Sendai, Miyagi 980-8579, Japan)
資料名： Journal of Magnetism and Magnetic Materials  (Journal of Magnetism and Magnetic Materials)
巻： 552  ページ： Null  発行年： 2022年 
JST資料番号： H0644A  ISSN： 0304-8853  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： SmFe_12ベース粉末の顕著な固有硬磁性は,実用化のために外因性特性に変換するのが難しい。特に,非磁性粒界相に依存し,市販のNd_2Fe_14B系中の高保磁力を誘起するのに重要である従来の磁気分離構造が,まだ完成していないので,保磁力は不十分である。本研究では,SmFe_10V_2粉末に非磁性Smリッチ層を与える還元拡散過程による磁気分離を達成するための新しいアプローチを示した。SmFe_10V_2粉末を囲むこのSmリッチ層の最適試料は744.9kA/mの高い保磁力と61.7Am2/kgの中程度の最大磁化を有した。相キャラクタリゼーションと微細構造観察に基づいて,主なSmFe_10V_2磁気相はよく維持され,周囲のSmリッチ層は磁気相を分離し,隣接磁性相の強磁性相互作用を弱め,高い保磁力に寄与する。本研究では,非磁性層を導入することによって,高保磁力磁性粉末を開発する新しい方法を示した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *保磁力 ,  磁化 ,  微細構造 ,  *粉体 ,  永久磁石 ,  磁気 ,  磁力分離 ,  性徴 ,  キャラクタリゼーション ,  拡散過程
準シソーラス用語： 硬磁性 ,  磁性相 ,  強磁性相互作用 ,  非磁性 ,  高保磁力 , 【Automatic Indexing@JST】

著者キーワード (5件)： 永久磁石 ,  ThMn_12 ,  SmFe_12 ,  保磁力 ,  還元拡散

分類 (1件)： 金属結晶の磁性  (BM06040T)

タイトルに関連する用語 (6件)： 還元 ,  拡散プロセス ,  調製 ,  Sm ,  高保磁力 ,  粉末