広い周囲温度範囲におけるNi Cu Mn Ga合金の高減衰能【Powered by NICT】

High damping capacity of a Ni-Cu-Mn-Ga alloy in wide ambient-temperature range

著者 (15件)： Liao Xiaoqi (MOE Key Laboratory for Nonequilibrium Synthesis and Modulation of Condensed Matter, Xi’an Jiaotong University, Xi’an 710049, China) ,  Liao Xiaoqi (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China) ,  Wang Yu (MOE Key Laboratory for Nonequilibrium Synthesis and Modulation of Condensed Matter, Xi’an Jiaotong University, Xi’an 710049, China) ,  Wang Yu (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China) ,  Fan Genlian (State Key Lab for Metal Matrix Composites, Shanghai Jiaotong University, Shanghai 200240, China) ,  Liu Enke (State Key Laboratory for Magnetism, Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China) ,  Shang Jiaruo (MOE Key Laboratory for Nonequilibrium Synthesis and Modulation of Condensed Matter, Xi’an Jiaotong University, Xi’an 710049, China) ,  Shang Jiaruo (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China) ,  Yang Sen (MOE Key Laboratory for Nonequilibrium Synthesis and Modulation of Condensed Matter, Xi’an Jiaotong University, Xi’an 710049, China) ,  Yang Sen (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China) ,  Luo Hongzhi (School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130, China) ,  Song Xiaoping (MOE Key Laboratory for Nonequilibrium Synthesis and Modulation of Condensed Matter, Xi’an Jiaotong University, Xi’an 710049, China) ,  Song Xiaoping (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China) ,  Ren Xiaobing (National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, 305-0047, Ibaraki, Japan) ,  Otsuka Kazuhiro (National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, 305-0047, Ibaraki, Japan)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 695  ページ： 2400-2405  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Ni_55 xCu_xMn_25Ga_20(x=0, 2, 4, 6)形状記憶合金の減衰能を詳細に研究した。結果はCu含有量の増加と共に増加する減衰ピーク容量を示した。特に,0.08のピーク値を有する高減衰ピークはNi_49Cu_6Mn_25Ga_20合金,173K TI425の広い温度範囲に渡り広がるのが判明した。第一原理計算は,Niに対するCuの置換はNi_55 xCu_xMn_25Ga_20のp-d軌道混成を弱め,そのマルテンサイト率,その双晶境界移動度と減衰能力を高めるを減少させるを示した。著者らの研究は,常温高減衰合金の開発に光を当てた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： マルテンサイト ,  *ニッケル ,  *合金 ,  双晶境界 ,  ピーク値 ,  *銅 ,  形状記憶合金 ,  移動度 ,  配位混合 ,  第一原理計算 ,  *温度範囲 ,  ピーク容量 ,  Cu含有量

著者キーワード (5件)： 強磁性形状記憶合金 ,  マルテンサイト相変態 ,  減衰 ,  磁気的性質 ,  動的機械分析

分類 (2件)： その他の金属組織学  (WB01040Y) ,  磁気的性質  (WB02020J)

タイトルに関連する用語 (6件)： 周囲温度 ,  Ni ,  Cu ,  Mn ,  Ga合金 ,  減衰能