引張変形中のβ型チタン合金における変形に誘起されたω相変態【Powered by NICT】

Deformation-induced ω-phase transformation in a β-type titanium alloy during tensile deformation

著者 (8件)： Liu Huihong (Joining and Welding Research Institute, Osaka University, Ibaraki, Osaka 567-0047, Japan) ,  Niinomi Mitsuo (Institute for Materials Research, Tohoku University, Sendai, Miyagi 980-8577, Japan) ,  Niinomi Mitsuo (Graduate School of Engineering, Osaka University, Suita, Osaka 565-0871, Japan) ,  Niinomi Mitsuo (Graduate School of Science and Technology, Meijyo University, Nagoya, Aichi 468-8502, Japan) ,  Niinomi Mitsuo (Institute of Materials and Systems for Sustainability, Nagoya University, Nagoya, Aichi 464-8603, Japan) ,  Nakai Masaaki (Department of Mechanical Engineering, Faculty of Science and Engineering, Kindai University, Higashiosaka, Osaka 577-8502, Japan) ,  Cho Ken (Graduate School of Engineering, Osaka University, Suita, Osaka 565-0871, Japan) ,  Fujii Hidetoshi (Joining and Welding Research Institute, Osaka University, Ibaraki, Osaka 567-0047, Japan)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 130  ページ： 27-31  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 引張変形中の変形誘起ω相変換を開発し脊髄支援合金,Ti9Cr 2で調べた。[0001]方向に沿って優先的に単一バリアントω変態と均一に分布したω粒子の成長および/または組立の両方が引張変形中の合金の受ける。はこの変形誘起ω相変態が塑性変形を伴わない弾性歪あるいは応力により誘発されることを確認した。さらに,再配向プロセスがこの変換に働く,ω_1変異体は外部荷重条件に関連する可能性のある{001}<110>双晶型機構とω相とβ相の方位によるω_2変異体に再配向可能性がある。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *合金 ,  *チタン合金 ,  塑性変形 ,  双晶 ,  *ω相 ,  β相 ,  脊髄 ,  再配向 ,  *引張変形 ,  荷重条件 ,  弾性歪

著者キーワード (4件)： 相変態 ,  チタン合金 ,  透過型電子顕微鏡観察 ,  引張変形

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： 引張変形 ,  β型チタン合金 ,  誘起 ,  相変態