Effect of MgO powder addition to alkali and alkaline-earth borosilicate glass paste on the acid durability and peel adhesion characteristics of Ag conductors formed with the glass paste

ガラスペーストで形成したAg導体の耐酸性と剥離粘着力特性に及ぼすアルカリおよびアルカリ土類ホウケイ酸ガラスペーストへのMgO粉末添加の影響

Author (4)： TACHIBANA Yusuke (DuPont Electronics Center, DuPont Electronic Materials, K. K.) ,  TACHIBANA Yusuke (Department of Materials Science and Engineering, Tokyo Institute of Technology) ,  MATSUDA Akifumi (Department of Materials Science and Engineering, Tokyo Institute of Technology) ,  YOSHIMOTO Mamoru (Department of Materials Science and Engineering, Tokyo Institute of Technology)
Material： Journal of the Ceramic Society of Japan (Web)  (J Ceram Soc Jpn (Web))
Volume： 128  Issue： 3  Page： 142-148(J-STAGE)  Publication year： 2020 
JST Material Number： U0409A  ISSN： 1348-6535  Document type： Article
Article type： 原著論文  Country of issue： Japan (JPN)  Language： ENGLISH (EN)

Thesaurus term： *borosilicate glass ,  alkali metal compound ,  alkaline earth metal compound ,  magnesium oxide ,  *additive effect ,  *paste ,  conductor material ,  silver ,  acid resistance ,  exfoliation ,  adhesive force ,  alumina ,  substrate(plate) ,  powder ,  thick film ,  firing(heat treatment) ,  crystallization ,  microcrystal ,  surface crack ,  sulfuric acid ,  aqueous solution ,  peeling test

Author keywords (8)： Borosilicate glass ,  Glass paste ,  Chemical durability ,  Crystallization ,  Acid corrosion ,  Ag conductor paste ,  Thick-film ,  Peel adhesion

JST classification (2)： Properties,analysis and test of glass  (YC02030Z) ,  Conducting materials  (NA04020L)

Reference (22)：

• 1) J. R. Larry, R. M. Rosenberg and R. O. Uhler, IEEE T. Compon. Hybr., 3, 211-225 (1980).
• 2) M. V. Coleman and G. E. Gurnett, Electrocomp. Sci. Tech., 5, 55-59 (1978).
• 3) B. E. Taylor, J. J. Felten, S. J. Horowitz, J. R. Larry and R. M. Rosenberg, Electrocomp. Sci. Tech., 9, 67-85 (1981).
• 4) J. Savage, “Handbook of thick film technology”, Ed. by P. J. Holmes and R. G. Loasby, Electrochemical publications Ltd., Scotland (1976) pp. 97-113.
• 5) R. Terai, Mater. Integr., 17, 51-55 (2004).

Terms in the title (11)： ガラス ,  ペースト ,  Ag ,  導体 ,  耐酸性 ,  粘着力 ,  アルカリ ,  アルカリ土類 ,  ホウケイ酸ガラス ,  MgO ,  粉末