ナノインデンテーションを用いたマグネシウムのナノオーダー摩耗特性

Nano-Ordered Wear Property of Magnesium Obtaining Nanoindentation

著者 (6件)： SOMEKAWA Hidetoshi (National Inst. for Materials Sci., Res. Center for Strategic Materials, 1-2-1 Sengen, 305-0047, Tsukuba, Ibaraki, JPN) ,  TOMITA Kazuhiro (Doshisha Univ., Dep. of Mechanical Engineering, 1-3 Miyakodani, Tatara, 610-0321, Kyotanabe, Kyoto, JPN) ,  TODA Miwako (Doshisha Univ., Dep. of Mechanical Engineering, 1-3 Miyakodani, Tatara, 610-0321, Kyotanabe, Kyoto, JPN) ,  HIRAYAMA Tomoko (Doshisha Univ., Dep. of Mechanical Engineering, 1-3 Miyakodani, Tatara, 610-0321, Kyotanabe, Kyoto, JPN) ,  HIRAYAMA Tomoko (Japan Sci. and Technol. Agency, PRESTO, 4-1-8 Honcho, 332-0012, Kawaguchi, Saitama, JPN) ,  MATSUOKA Takashi (Doshisha Univ., Dep. of Mechanical Engineering, 1-3 Miyakodani, Tatara, 610-0321, Kyotanabe, Kyoto, JPN)
資料名： Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science  (Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science)
巻： 46  号： 9  ページ： 4351-4359  発行年： 2015年09月 
JST資料番号： E0265B  ISSN： 1073-5623  CODEN： MTTABN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 単結晶及び多結晶マグネシウムのナノスケールの摩耗特性を,ナノインデンテーション法を用いて調べた。単結晶の結果から,例えば低い印加荷重の条件下のような変形双晶が全く形成されない場合,結晶配向性は摩耗速度に影響することが分かった。しかし,スクラッチ試験中に変形双晶が形成した場合,摩耗特性が悪くなり,摩耗速度が増加した。1つの理由は,双晶境界が転位ソースとシンクとしての役割を果さず,双晶境界での転位は変形双晶の拡大と成長をもたらしたことであった。摩耗特性への粒界の影響については,微細なマグネシウムの摩耗速度は,単結晶のそれと同様であった。この結果は,結晶粒界の存在が,Pin-on-Disk配置のような大規模な摩耗試験のように,マグネシウムの摩耗特性を有効に改善しないことを示した。Copyright 2015 The Minerals, Metals & Materials Society and ASM International Translated from English into Japanese by JST.

シソーラス用語： *マグネシウム ,  ナノインデンテーション ,  *摩耗特性 ,  単結晶 ,  多結晶 ,  変形双晶 ,  双晶境界 ,  結晶粒界 ,  摩耗試験 ,  摩耗速度 ,  転位【結晶】 ,  試験装置 ,  摩擦試験
準シソーラス用語： ピンオンディスク型試験機

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： ナノインデンテーション ,  マグネシウム ,  ナノオーダー ,  摩耗特性