Surface integrity of 2304 duplex stainless steel after different grinding operations

異なる研削作業後の2304二相ステンレス鋼の表面の健全性

Author (3)： Zhou Nian (Department of Material Science, Dalarna University, SE-79188 Falun, Sweden and KTH, SE-10044 Stockholm, Sweden) ,  Peng Ru Lin (Department of Management and Engineering, Linkoping University, SE-58183 Linkoping, Sweden) ,  Pettersson Rachel (Jernkontoret, SE-11187 Stockholm, Sweden and KTH, SE-10044 Stockholm, Sweden)
Material： Journal of Materials Processing Technology  (J Mater Process Technol)
Volume： 229  Page： 294-304  Publication year： Mar. 2016 
JST Material Number： H0650A  ISSN： 0924-0136  Document type： Article
Article type： 原著論文  Country of issue： Netherlands (NLD)  Language： ENGLISH (EN)

Thesaurus term： *grinding ,  *duplex stainless steel ,  residual stress ,  *surface roughness ,  surface defect ,  abrasive grain ,  machining force ,  Lubrication ,  surface course ,  tensile stress ,  fatigue ,  stress corrosion cracking ,  grinding force ,  *surface integrity ,  crack ,  corrosion cracking
Semi thesaurus term： 2304鋼 ,  *surface integrity

Author keywords (4)： Surface integrity ,  Grinding ,  Duplex stainless steel 2304 ,  Residual stress