Al-Mg-Si-Cu合金の溶体化処理間の析出物の溶解

Dissolution of Precipitates During Solution Treatment of Al-Mg-Si-Cu Alloys

著者 (4件)： Zhang Xukai (State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, P.R. China) ,  Guo Mingxing (State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, P.R. China) ,  Zhang Jishan (State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, P.R. China) ,  Zhuang Linzhong (State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, P.R. China)
資料名： Metallurgical and Materials Transactions. B. Process Metallurgy and Materials Processing Science  (Metallurgical and Materials Transactions. B. Process Metallurgy and Materials Processing Science)
巻： 47  号： 1  ページ： 608-620  発行年： 2016年02月 
JST資料番号： E0411B  ISSN： 1073-5615  CODEN： MTTBCR  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 単一の球状粒子に対する古典的拡散律速溶解方程式と Johnsen-MehlはAvrami方程式を組み合わせたモデルを,Al-Mg-Si-Cu合金中に含む種々の種類の析出物(Si,Mg₂Si,Q(Al_1.9Mg_4.1Si_3.3Cu))の溶解プロセスの扱いに使用した。結果は,合金マトリックス中のサイズおよび溶質濃度が増加するにつれて,析出物の溶解時間が増加することを示した。同じサイズと濃度の場合,それらの溶解時間はSi>Q(Al_1.9Mg_4.1Si_3.3Cu)>Mg₂Siの順であった。冷間圧延されたAl-Mg-Si-Cu合金において,約700nmの大きさの2つの析出物(Mg₂Si及びAl_1.9Mg_4.1Si_3.3Cuが得られ,完全溶解時間は約15秒であり,開発したモデルによる計算時間と同じだった。溶解時間の理論的予測は,Al-Mg-Si-Cu合金の溶体化処理および加工熱処理パラメータの設計に大いに使用することができる。Copyright 2015 The Minerals, Metals & Materials Society and ASM International Translated from English into Japanese by JST.

シソーラス用語： *アルミニウム合金 ,  マグネシウム含有合金 ,  ケイ素含有合金 ,  銅含有合金 ,  *溶体化処理 ,  *析出物 ,  *溶解 ,  *固溶体 ,  *粒子 ,  *拡散律速 ,  *レート方程式 ,  熱処理条件 ,  硬度 ,  金属組織 ,  *球状粒子 ,  組織

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (7件)： Al ,  Mg ,  Si ,  Cu合金 ,  溶体化処理 ,  析出物 ,  溶解