酸化中の正常スペクトル放射率に及ぼすNi基合金DZ125の効果の研究【Powered by NICT】

Investigation of the effects of Ni-based alloy DZ125 on the normal spectral emissivity during oxidation

著者 (6件)： Zhao Shunan (Institute of Engineering Thermophysics, Chinese Academy of Sciences, Beijing 100190, China) ,  Zhao Shunan (University of the Chinese Academy of Sciences, Beijing 100049, China) ,  Li Xunfeng (Institute of Engineering Thermophysics, Chinese Academy of Sciences, Beijing 100190, China) ,  Zhou Xiaoming (Institute of Engineering Thermophysics, Chinese Academy of Sciences, Beijing 100190, China) ,  Cheng Keyong (Institute of Engineering Thermophysics, Chinese Academy of Sciences, Beijing 100190, China) ,  Huai Xiulan (Institute of Engineering Thermophysics, Chinese Academy of Sciences, Beijing 100190, China)
資料名： Applied Thermal Engineering  (Applied Thermal Engineering)
巻： 109  号： PA  ページ： 663-671  発行年： 2016年 
JST資料番号： E0667B  ISSN： 1359-4311  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 酸化中のNi基合金DZ125の正常スペクトル放射率は波長1.35~2.35μm以上の空気中で12hの810%,916%および998°Cで実験的に測定した。垂直分光放射率の複合標準不確実性は3%以下であった。放射率の振動と放射率に及ぼす酸化温度,加熱時間と波長の影響を調べた。放射率の振動は基板と酸化皮膜の表面間の放射の干渉効果により形成される。酸化プロセスとして大きな波長に対する放射率シフトの干渉極値が進行する。結果よると,基準スペクトル放射率は,温度の上昇および放射率の振動の発生を除いて波長の減少とともに基本的に増加することを示した。垂直分光放射率は,初期加熱時間で急激に増加しており,酸化は飽和しようとするとき,放射率の変化は遅くなる。に加えて,放射率適合モデル対加熱時間と波長を確立し,それは実験データと良く一致した。フィッティングモデルの放射率相対誤差は3%以下であった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *放射率 ,  *分光放射率 ,  干渉 ,  *ニッケル合金 ,  波長 ,  不確実性 ,  酸化膜 ,  酸化 ,  相対誤差 ,  加熱時間 ,  化成皮膜
準シソーラス用語： 干渉効果 , 【Automatic Indexing@JST】

著者キーワード (4件)： Ni基合金DZ125 ,  酸化 ,  正常スペクトル放射率 ,  フィッティングモデル

分類 (1件)： 対流・放射熱伝達  (PA02030K)

タイトルに関連する用語 (4件)： 酸化 ,  スペクトル放射率 ,  Ni基合金 ,  研究