連続鋼線で強化したマグネシウムの圧縮特性と減衰能【Powered by NICT】

Compressive properties and damping capacities of magnesium reinforced with continuous steel wire

著者 (3件)： Li Qiuyan (Shanghai Key Laboratory of Materials Laser Processing and Modification, and State Key Lab of Metal Matrix Composites, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China) ,  Li Jiao (College of Foreign Studies, Jinan University, Guangzhou 510632, China) ,  He Guo (Shanghai Key Laboratory of Materials Laser Processing and Modification, and State Key Lab of Metal Matrix Composites, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 680  ページ： 92-96  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 連続304ステンレス鋼線(304/Mg)で強化したマグネシウムは,溶浸鋳造プロセスを用いて作製した。304/mgを新しい内部構造を有していた。304/mgの圧縮特性と減衰特性を試験した。304/mgの応力-ひずみ曲線は金属ゴムのそれに類似していた。304/mgの圧縮強度と弾性率は純Mgのそれよりも42.8%および55.6%高かった。304/mgのエネルギー吸収能は純Mgのそれの2.5倍であった。動的機械分析(DMA)試験は,純粋なMgの減衰能は低歪振幅で304/mgのそれよりも高いことを示した。二つの内部摩擦ピーク(P1とP2)温度依存減衰曲線を示した。304/mgのP1ピークはより低い温度にシフトし,P2ピークは純Mgのそれと比較して,より高い温度にシフトした。304/mg複合材料の調製法はMgの減衰能と強度を改善するために参考になりうる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 機械的性質 ,  動的機械分析 ,  圧縮強さ ,  *マグネシウム ,  圧縮性 ,  溶浸 ,  応力歪曲線 ,  温度依存性 ,  複合材料 ,  エネルギー吸収 ,  内部摩擦 ,  鋼線 ,  弾性係数 ,  減衰特性 ,  金属線 ,  性質 ,  強度 ,  曲線 ,  線

著者キーワード (5件)： 複合材料 ,  マグネシウム ,  ワイヤ ,  機械的性質 ,  減衰