Zr-Excel合金の準安定相と重イオン(Kr²⁺)照射下の安定性

Metastable phases in Zr-Excel alloy and their stability under heavy ion (Kr²⁺) irradiation

著者 (6件)： Yu Hongbing (Department of Mechanical and Materials Engineering, Queen’s University, Kingston, ON, K7L 3N6, Canada) ,  Zhang Ken (Department of Mechanical and Materials Engineering, Queen’s University, Kingston, ON, K7L 3N6, Canada) ,  Yao Zhongwen (Department of Mechanical and Materials Engineering, Queen’s University, Kingston, ON, K7L 3N6, Canada) ,  Kirk Mark A. (Material Science Division Argonne National Laboratory, Argonne, IL, 60439, USA) ,  Long Fei (Department of Mechanical and Materials Engineering, Queen’s University, Kingston, ON, K7L 3N6, Canada) ,  Daymond Mark R. (Department of Mechanical and Materials Engineering, Queen’s University, Kingston, ON, K7L 3N6, Canada)
資料名： Journal of Nuclear Materials  (Journal of Nuclear Materials)
巻： 469  ページ： 9-19  発行年： 2016年02月 
JST資料番号： D0148A  ISSN： 0022-3115  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Zr-Excel合金(Zr-3.5Sn-0.8Nb-0.8Mo,wt.%)はCANDU-SCWR設計における圧力管の候補材料として提案された。シンクロトロンX線研究を用いて,Zr-Excel圧力管材料の準安定相の格子特性を調べた。重イオン(1MeV Kr²⁺)を200°C及び450°Cでその場照射し,原子炉環境下の準安定相の安定性を模擬した。何れの照射下でも,β-Zrの分解は観測されなかった。しかし,ω-Zr粒子は形状が変化し,200°C照射時にβ/ω界面でFeの濃縮に関係する収縮が生じたが,450°Cでは生じなかった。何れの照射でも,照射後にα基質中のFeレベルが顕著に上昇した。200°Cでは,ω相中のNb,Mo,Feが増加したが,β相では減少した。Copyright 2016 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ジルコニウム合金 ,  スズ含有合金 ,  ニオブ含有合金 ,  モリブデン含有合金 ,  軽水型原子炉 ,  原子炉材料 ,  X線回折 ,  *準安定相 ,  *重イオン照射 ,  微細構造 ,  電子顕微鏡観察 ,  エネルギー分散蛍光X線分析 ,  超臨界圧水冷却型原子炉
準シソーラス用語： SCWR型原子炉

著者キーワード (4件)： Zr-Excel alloy ,  Heavy ion irradiation ,  Phase stability ,  Chemi-STEM EDS

分類 (1件)： 金属の放射線による構造と物性の変化  (BK16122N)