予時効処理を施したAl-5.2Mg-45Cu-2.0Zn(wt%)合金の改良された時効硬化応答と変化した析出挙動【Powered by NICT】

Improved age-hardening response and altered precipitation behavior of Al-5.2Mg-0.45Cu-2.0Zn (wt%) alloy with pre-aging treatment

著者 (5件)： Cao Cheng (State Key Laboratory of Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, 100083, People’s Republic of China) ,  Zhang Di (State Key Laboratory of Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, 100083, People’s Republic of China) ,  Zhuang Linzhong (State Key Laboratory of Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, 100083, People’s Republic of China) ,  Zhuang Linzhong (Tata Steel, 1970 CA, IJmuiden, The Netherlands) ,  Zhang Jishan (State Key Laboratory of Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, 100083, People’s Republic of China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 691  ページ： 40-43  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,予時効処理は新たに開発したAl-5.2Mg-45Cu-2.0Zn合金上で行った。結果は合金の時効硬化応答は改良沈殿微細構造による予時効処理により顕著に改善されていることを示した。予備時効処理なしに,ピーク時効条件におけるミクロ組織は粗大なラス状T Mg_32(Al, Zn)49相と針状S Al_2MgCu相から成っていた。しかし,予時効処理とピーク時効条件における合金のミクロ組織はS相消失と微細で等軸T相の高い密度で構成されている。両種T相が同じ体心立方(BCC)Mg_32(Al, Zn)49型の構造(Im3, a=1.422 nm)を持つが,組成に大きな差を示した。予時効処理なしで180°Cでの時効中に合金の析出挙動の図式的説明は解析結果に従って行った。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： アルミニウム合金 ,  沈殿 ,  *合金 ,  微細構造 ,  *時効硬化 ,  *時効 ,  *アルミニウム ,  透過型電子顕微鏡法 ,  S相 ,  針状
準シソーラス用語： 原子プローブトモグラフィー ,  T相 , 【Automatic Indexing@JST】

著者キーワード (5件)： アルミニウム合金 ,  沈殿 ,  クラスタ ,  透過型電子顕微鏡観察 ,  原子プローブトモグラフィー

分類 (2件)： 組織的硬化現象  (WB01020C) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： 時効処理 ,  Al ,  合金 ,  時効硬化 ,  応答 ,  析出 ,  挙動