グラフェン酸化物膜の周期的マイクロブリッジ試験【Powered by NICT】

Cyclic microbridge testing of graphene oxide membrane

著者 (6件)： Wu Quan (Corrosion and Protection Center, Key Laboratory for Environmental Fracture (MOE), University of Science and Technology Beijing, Beijing 100083, China) ,  Dai Zhaohe (National Center for Nanoscience and Technology China, Beijing 100190, China) ,  Su Yanjing (Corrosion and Protection Center, Key Laboratory for Environmental Fracture (MOE), University of Science and Technology Beijing, Beijing 100083, China) ,  Volinsky Alex A. (Department of Mechanical Engineering, University of South Florida, Tampa, FL 33620, USA) ,  Liu Luqi (National Center for Nanoscience and Technology China, Beijing 100190, China) ,  Zhong Zhang (National Center for Nanoscience and Technology China, Beijing 100190, China)
資料名： Carbon  (Carbon)
巻： 116  ページ： 479-489  発行年： 2017年 
JST資料番号： H0270B  ISSN： 0008-6223  CODEN： CRBNA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： マイクロブリッジ試験の柔軟な膜変形を決定するために理論式は膜変形は伸長,曲げと反対に支配されているという仮定に基づいて導いた。マイクロブリッジ試料はパターン化したシリコン基板上に置かれた0.17μm厚の自立グラフェン酸化物膜から作製し,ナノインデンテーションシステムを用いて試験した。有効Young率は,両方の負荷と除荷中のマイクロブリッジ試験から決定した。フレキシブル膜理論式を組み合わせた変形可能な引張・せん断モデルを用いて,マルチスケールモデルは,グラフェン酸化物膜のせん断弾性率を決定するために提案した。異なる荷重配列のYoung率に及ぼす温度の影響を調べた。偏光Raman分光法およびX線回折を用いて,グラフェン酸化物膜の自己硬化挙動を特性化した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 引張 ,  変形 ,  Young率 ,  *グラフェン ,  剪断 ,  Raman分光法 ,  除荷 ,  *酸化膜 ,  パターン形成 ,  X線回折 ,  剛性率 ,  キャラクタリゼーション ,  シリコンウエハ ,  *化成皮膜
準シソーラス用語： 理論式 ,  *マイクロブリッジ , 【Automatic Indexing@JST】