PA66/SEBS-G-MAHブレンドの機械的性質と微細構造を研究した。【JST・京大機械翻訳】

MECHANICAL PROPERTY AND MICROCOSMIC STRUCTURE OF PA1111/SEBS-g-MAH BLENDS

著者 (9件)： Xu Yingqiang (School of Materials Science and Engineering, Zhengzhou University) ,  Yang Shaohui (School of Materials Science and Engineering, Zhengzhou University) ,  Li Zhaopeng (School of Materials Science and Engineering, Zhengzhou University) ,  Fu Canping (School of Materials Science and Engineering, Zhengzhou University) ,  Zhang Yanehang (School of Materials Science and Engineering, Zhengzhou University) ,  Fu Peng (School of Materials Science and Engineering, Zhengzhou University) ,  Liu Minying (School of Materials Science and Engineering, Zhengzhou University) ,  Wang Yudong (School of Materials Science and Engineering, Zhengzhou University) ,  Zhao Qingxiang (School of Materials Science and Engineering, Zhengzhou University)
資料名： Gongcheng Suliao Yingyong  (Gongcheng Suliao Yingyong)
巻： 37  号： 6  ページ： 24-26  発行年： 2009年 
JST資料番号： C2099A  ISSN： 1001-3539  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： マレイン酸無水物グラフト化スチレン(エチレン/エチレン/ブチレン/スチレン)共重合体(SEBS-G-MAH)を強化剤として用いて,一連のSEBS/SEBS-G-MAHブレンドを調製し,その機械的性質と微細構造を研究した。結果は,強化剤の含有量が増加するにつれて,ノッチ付衝撃強さが著しく増加し,強化剤の質量分率が25%のとき,衝撃強さは39.4KJ/M2であり,純粋なPAのそれの11.3倍であることを示した。微細構造の研究により、PA1111の断裂は靱性破壊に属し、PA1111//SEBS-G-MAH混合系の切欠き衝撃断面には明らかな応力白化現象があり、衝撃強度が向上する主な原因は応力集中点の増加による大量のクレージングの発生によるものであることが明らかになった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： クレーズ ,  衝撃強さ ,  *機械的性質 ,  衝撃 ,  *微細構造 ,  断裂 ,  応力集中 ,  切欠き ,  靱性 ,  混合系 ,  質量分率 ,  強度 ,  *性質

著者キーワード (3件)： PA1111 ,  SEBS-g-MAH ,  toughening

分類 (1件)： 機械的性質  (YH02022L)

タイトルに関連する用語 (4件)： ブレンド ,  機械的性質 ,  微細構造 ,  研究